広い温度範囲におけるバランスのとれた強度と延性を有する直接鋳造バルク共晶および共晶に近い高エントロピー合金【Powered by NICT】
Directly cast bulk eutectic and near-eutectic high entropy alloys with balanced strength and ductility in a wide temperature range
著者 (13件):
Lu Yiping
(Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China)
,
Gao Xuzhou
(School of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094, PR China)
,
Jiang Li
(Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China)
,
Chen Zongning
(Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China)
,
Wang Tongmin
(Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China)
,
Jie Jinchuan
(Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China)
,
Kang Huijun
(Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China)
,
Zhang Yubo
(Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China)
,
Guo Sheng
(Surface and Microstructure Engineering Group, Materials and Manufacturing Technology, Chalmers University of Technology, SE-41296 Gothenburg, Sweden)
,
Ruan Haihui
(Department of Mechanical Engineering, The Hong Kong Polytechnic University, Hung Hom, Hong Kong, China)
,
Zhao Yonghao
(School of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094, PR China)
,
Cao Zhiqiang
(Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China)
,
Li Tingju
(Key Laboratory of Solidification Control and Digital Preparation Technology (Liaoning Province), School of Materials Science and Engineering, Dalian University of Technology, Dalian 116024, PR China)
資料名:
Acta Materialia
(Acta Materialia)
巻:
124
ページ:
143-150
発行年:
2017年
JST資料番号:
A0316A
ISSN:
1359-6454
資料種別:
逐次刊行物 (A)
記事区分:
原著論文
発行国:
イギリス (GBR)
言語:
英語 (EN)