Effects of Welding Sequence on Residual Stress Distribution in Circumferential Welded Joints with X-shape Grooves

溶接金属の残留応力に及ぼす溶接順序の影響を研究した。【JST・京大機械翻訳】

Author (4)： Wan Haibo (Shanghai Power Equipment Research Institute) ,  Wang Yanfeng (Shanghai Power Equipment Research Institute) ,  Li Qiang (Shanghai Power Equipment Research Institute) ,  Tang Bin (Wujing Thermal Power Plant, Shanghai Electric Power Co., Ltd.)
Material： Dongligongcheng Xuebao
Volume： 36  Issue： 8  Page： 664-670  Publication year： 2016 
JST Material Number： C2678A  ISSN： 1674-7607  Document type： Article
Article type： 原著論文  Country of issue： China (CHN)  Language： CHINESE (ZH)

Abstract/Point： Using ABAQUS software, a 2D ax...

Register(free) or Log In to access     To see more with JDream III (charged).   {{ this.onShowAbsJLink("http://jdream3.com/lp/jglobal/index.html?docNo=17A0109700&from=J-GLOBAL&jstjournalNo=C2678A") }}

Thesaurus term： welded joint ,  stress corrosion cracking ,  stainless steel ,  *welding ,  tensile stress ,  two dimension ,  cylinder(hollow body) ,  compressive stress ,  axial symmetry ,  *weld metal ,  axial stress ,  hoop stress ,  *residual stress
Semi thesaurus term： ABAQUS ,  有限要素 , 【Automatic Indexing@JST】

Author keywords (4)： X-shaped groove ,  welding sequence ,  stress corrosion cracking ,  finite element simulation

JST classification (1)： Weld zone  (WC07100I)

Terms in the title (3)： 溶接金属 ,  残留応力 ,  研究