Research Progress on Cracking Mechanism and Control of Laser Additive Repaired Nickel-based Superalloys with High Content of Al+Ti

高AL+TI基超合金のレーザアブレーションによる液化亀裂の形成機構と制御研究の進展をレビューした。【JST・京大機械翻訳】

Author (7)： Li Qiuge (State Key Laboratory of Solidification Processing,Northwestern Polytechnical University) ,  Lin Xin (State Key Laboratory of Solidification Processing,Northwestern Polytechnical University) ,  Wang Xinghua (Luoyang Ship Material Research Institute) ,  Liu Fenggang (State Key Laboratory of Solidification Processing,Northwestern Polytechnical University) ,  Liu Fencheng (National Defence Key Discipline Laboratory of Light Alloy Processing Science and Technology,Nanchang Hangkong University) ,  Yang Haiou (State Key Laboratory of Solidification Processing,Northwestern Polytechnical University) ,  Huang Weidong (State Key Laboratory of Solidification Processing,Northwestern Polytechnical University)
Material： Yingyong Jiguang  (Applied Laser)
Volume： 36  Issue： 4  Page： 471-477  Publication year： 2016 
JST Material Number： C2473A  ISSN： 1000-372X  Document type： Article
Article type： 原著論文  Country of issue： China (CHN)  Language： CHINESE (ZH)

Abstract/Point： Nickel-based superalloys with ...

Register(free) or Log In to access     To see more with JDream III (charged).   {{ this.onShowAbsJLink("http://jdream3.com/lp/jglobal/index.html?docNo=17A0067683&from=J-GLOBAL&jstjournalNo=C2473A") }}

Thesaurus term： high temperature ,  *laser ablation ,  high temperature strength ,  *liquefaction (phase transition) ,  corrosion resistance ,  *crack ,  *alloy ,  *superalloy ,  *laser ,  aero engine ,  mechanical property ,  strength
Semi thesaurus term： 敏感性 ,  航空宇宙 ,  長期使用 ,  使用環境 ,  *形成機構 , 【Automatic Indexing@JST】

Author keywords (4)： laser additive repairing ,  nickel-based superalloys with high content of Al+Ti ,  cracking mechanism ,  crack control

JST classification (1)： Laser irradiation effects and damages  (BK16040S)

Terms in the title (7)： 超合金 ,  レーザアブレーション ,  液化 ,  亀裂 ,  研究 ,  進展 ,  レビュー