規則性立方晶Zr添加メソ多孔性シリカのEISA(気化誘起自己組織化)法による調製と構造特性化

Preparation and Structure Characterization of Ordered Cubic Zr-doped Mesoporous Silica by EISA Method

著者 (7件)： CHU Bin (State Key Lab. of Inorganic Synthesis and Preparative Chemistry, Jilin Univesity, Changchun) ,  WANG RunWei (State Key Lab. of Inorganic Synthesis and Preparative Chemistry, Jilin Univesity, Changchun) ,  SHEN QiHui (State Key Lab. of Inorganic Synthesis and Preparative Chemistry, Jilin Univesity, Changchun) ,  CHEN Lu (State Key Lab. of Inorganic Synthesis and Preparative Chemistry, Jilin Univesity, Changchun) ,  WAN LiFeng (State Key Lab. of Inorganic Synthesis and Preparative Chemistry, Jilin Univesity, Changchun) ,  ZHU GuangShan (State Key Lab. of Inorganic Synthesis and Preparative Chemistry, Jilin Univesity, Changchun) ,  QIU ShiLun (State Key Lab. of Inorganic Synthesis and Preparative Chemistry, Jilin Univesity, Changchun)
資料名： Gaodeng Xuexiao Huaxue Xuebao  (Gaodeng Xuexiao Huaxue Xuebao)
巻： 28  号： 8  ページ： 1428-1430  発行年： 2007年 
JST資料番号： C2116A  ISSN： 0251-0790  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： EISA(気化誘起自己組織化)法により,構造指示剤としてトリブロック共重合体(Pluronic P123)を用い,高規則性立方晶Zr添加メソ多孔性シリカを直接調製した。小角粉末X線回折(XRD),透過型電子顕微鏡(TEM),窒素吸着により,メソ多孔性材料を特性化した。結果で,生成物は空間群Fd3nの面心立方構造を持つことを示した。N_2吸着で,Zr添加メソ多孔性シリカは,規則性構造に加え,均一孔サイズ(4.0nm)のみならず高表面積(550m2/g),大きな孔体積(0.66cm3/g)を持つことを明らかにした。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： *多孔質体 ,  *立方晶系 ,  規則度 ,  *自己組織化 ,  非イオン界面活性剤 ,  トリブロック共重合体 ,  ドーパント ,  *ジルコニウム ,  X線回折 ,  透過型電子顕微鏡 ,  吸着 ,  窒素 ,  空間群 ,  直径 ,  表面積 ,  体積 ,  *二酸化ケイ素 ,  *メソポーラスシリカ
準シソーラス用語： *シリカ ,  Pluronic P123 ,  規則性 ,  口径

分類 (3件)： 合成鉱物  (CD01040K) ,  非金属元素とその化合物の結晶構造  (BK07010N) ,  吸着剤  (YB03000W)

タイトルに関連する用語 (12件)： 規則性 ,  立方晶 ,  Zr ,  メソ多孔性 ,  シリカ ,  EISA ,  気化 ,  誘起 ,  自己組織化 ,  法 ,  調製 ,  構造特性