文献

J-GLOBAL ID：200902289043436998   整理番号：09A0402121

青-緑色発光蛍光体CaSc₂O₄:Tb³⁺: 交差緩和により操作されるルミネセンス

Blue-Green-Emitting Phosphor CaSc₂O₄:Tb³⁺: Tunable Luminescence Manipulated by Cross-Relaxation

著者 (7件)： HAO Zhendong (Changchun Inst. of Optics, Fine Mechanics and Physics, Chinese Acad. of Sci., Changchun, CHN) ,  HAO Zhendong (Graduate School, Chinese Acad. of Sci., Beijing, CHN) ,  ZHANG Jiahua (Changchun Inst. of Optics, Fine Mechanics and Physics, Chinese Acad. of Sci., Changchun, CHN) ,  ZHANG Xia (Changchun Inst. of Optics, Fine Mechanics and Physics, Chinese Acad. of Sci., Changchun, CHN) ,  LU Shaozhe (Changchun Inst. of Optics, Fine Mechanics and Physics, Chinese Acad. of Sci., Changchun, CHN) ,  WANG Xiaojun (Changchun Inst. of Optics, Fine Mechanics and Physics, Chinese Acad. of Sci., Changchun, CHN) ,  WANG Xiaojun (Georgia Southern Univ., Georgia, USA)
資料名： Journal of the Electrochemical Society  (Journal of the Electrochemical Society)
巻： 156  号： 3  ページ： H193-H196  発行年： 2009年 
JST資料番号： C0285A  ISSN： 1945-7111  CODEN： JESOAN  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 青-緑色蛍光体のCaSc₂O₄:xTb³⁺(x=0.01~0.12)を固相反応により合成した。近紫外光(254,276nm)で励起すると,これらの蛍光体は青色発光(350~480nm)と緑色発光(480~650nm)を同時に示した。前者はTb³⁺の⁵D₃→⁷F_J(J=3,4,5,6)遷移に,後者は⁵D₄→⁷F_J(J=3,4,5,6)遷移によるものである。⁵D₃から⁵D₄への交差緩和のために,Tb³⁺濃度(x)が増すにつれて青色光強度が減少し,緑色光強度が増大して発色光が変化した。交差緩和効率はxとともに増大し,x=0.12で84%に達した。この蛍光体と赤色蛍光体のCaSc₂O₄:Eu³⁺を混合すると蛍光ランプ用の白色蛍光体が得られる。

シソーラス用語： *蛍光体 ,  酸化物 ,  カルシウム化合物 ,  *スカンジウム化合物 ,  テルビウム ,  発光中心 ,  濃度依存性 ,  固相反応 ,  交差緩和 ,  *光ルミネセンス ,  可視発光スペクトル ,  スペクトル線強度 ,  色度

分類 (2件)： 無機化合物のルミネセンス  (BM08093J) ,  塩基,金属酸化物  (CD01030Z)

タイトルに関連する用語 (5件)： 青 ,  緑色発光 ,  蛍光体 ,  交差緩和 ,  ルミネセンス