PEDOT-PSS/PVA複合繊維の構造及び特性に及ぼす延伸倍率の影響

Effect of draw ratios on the structure and properties of PEDOT-PSS/PVA composite fibers

著者 (5件)： Xu Yingtao (Beijing Key Lab. of Clothing Materials R & D and Assessment, School of Materials Sci. & Engineering,Beijing Inst. of ...) ,  Li Xin (Beijing Key Lab. of Clothing Materials R & D and Assessment, School of Materials Sci. & Engineering,Beijing Inst. of ...) ,  Li Xiaoning (Beijing Key Lab. of Clothing Materials R & D and Assessment, School of Materials Sci. & Engineering,Beijing Inst. of ...) ,  Wang Rui (Beijing Key Lab. of Clothing Materials R & D and Assessment, School of Materials Sci. & Engineering,Beijing Inst. of ...) ,  Yang Zhongkai (Beijing Key Lab. of Clothing Materials R & D and Assessment, School of Materials Sci. & Engineering,Beijing Inst. of ...)
資料名： Fuhe Cailiao Xuebao  (Fuhe Cailiao Xuebao)
巻： 29  号： 3  ページ： 111-116  発行年： 2012年 
JST資料番号： C2466A  ISSN： 1000-3851  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 高電導性,良好な機械的特性及び良好な紡糸性挙動を有する複合導電性繊維を,ポリビニルアルコールと混合したポリ(3,4-エチレンジオキシチオフェン)-ポリスチレンスルホン酸(PEDOT-PSS)に基づく湿式紡糸によって得た。延伸倍率が繊維の導電性,構造,熱安定性及び機械的特性に及ぼす影響を調べた。その結果,延伸倍率が増加すると,PEDOT-PSS/PVA複合繊維上の微小繊維の数は増加し,その結晶性,熱安定性及び機械的特性は全て改良されることが判明した。PEDOT-PSS/PVA複合繊維の延伸倍率が4.0である場合には,その破断強度,引張り伸度及び初期弾性率はそれぞれ6.74cN/dtex,5.95%及び42.43cN/dtexで,その導電性は34.5S/cmに達し,良好な実用性を示した。Data from the ScienceChina, LCAS. Translated by JST

シソーラス用語： ポリエチレンジオキシチオフェン ,  ポリスチレンスルホン酸 ,  ポリビニルアルコール ,  *複合繊維 ,  *延伸 ,  湿式紡糸 ,  導電性 ,  熱安定性 ,  機械的性質