UV重合自己架橋ポリアクリル酸の吸水樹脂の調製および特性化【JST・京大機械翻訳】

UV polymerization and characterization of self-crosslinking polyacrylic acid superabsorbent

著者 (5件)： Mamatjan Yimit (Key Laboratory of Oil and Gas Fine Chemicals, Ministry of Education and Xinjiang Uyghur Autonomous Region, College of Chemistry and Chemical Engineering, Xinjiang University) ,  Amatjan Sawut (Key Laboratory of Oil and Gas Fine Chemicals, Ministry of Education and Xinjiang Uyghur Autonomous Region, College of Chemistry and Chemical Engineering, Xinjiang University) ,  Ismayil Nurulla (Key Laboratory of Oil and Gas Fine Chemicals, Ministry of Education and Xinjiang Uyghur Autonomous Region, College of Chemistry and Chemical Engineering, Xinjiang University) ,  Shi Qingdong (Key Laboratory of Xinjiang Oasis Ecology,College of Resources and Environmental Sciences, Xinjiang University) ,  Xu Wanting (Key Laboratory of Xinjiang Oasis Ecology,College of Resources and Environmental Sciences, Xinjiang University)
資料名： Gongneng Cailiao  (Gongneng Cailiao)
巻： 47  号： 4  ページ： 4182-4186  発行年： 2016年 
JST資料番号： C2095A  ISSN： 1001-9731  CODEN： GOCAEA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： アクリル酸を原料として,紫外線を用いて重合を開始する自己架橋ポリアクリル酸の吸水樹脂(PAASC)を調製した。IR、1H NMR,SEM法を用いて樹脂の構造についてキャラクタリゼーションを行った。この特性に及ぼす異なるパワーの紫外光源の照射距離および反応温度影響を研究した。その結果,紫外線パワーはW1、重合温度15°C、照射時間は40MIN、照射距離が15CMであるときに,調製した樹脂の吸水率は,吸水が最も良いであったが,吸収率は4/Gである塩水準は 206G/Gであった。吸着から,一片の。同時に,加圧条件下で異なる保水剤の吸水率の比較を行った。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： *吸水 ,  吸着 ,  *ポリアクリル酸 ,  *キャラクタリゼーション ,  加圧 ,  紫外光源 ,  吸水率 ,  反応温度 ,  *重合 ,  吸収係数 ,  紫外線 ,  脂肪族カルボン酸 ,  ビニル化合物 ,  不飽和カルボン酸
準シソーラス用語： 保水剤 ,  照射時間 ,  重合温度 , 【Automatic Indexing@JST】

著者キーワード (4件)： superabsorbent ,  UV polymerization ,  self-crosslinking polyacrylic acid ,  absorbency under load

分類 (2件)： 充填剤,補強材  (YH05030J) ,  共重合  (CG04030D)

物質索引 (1件)： アクリル酸

タイトルに関連する用語 (7件)： 重合 ,  自己 ,  架橋 ,  ポリアクリル酸 ,  吸水 ,  調製 ,  特性化