高速圧延小型Ti-6Al-4V合金棒の熱処理プロセス【Powered by NICT】

Heat treatment process of high-speed rolling small size Ti-6Al-4V alloys bar

著者 (6件)： Ding Hui (School of Materials Sci. and Engineering, Kunming Univ. of Sci. and Technol., Engineering Technol. Res. Center of ...) ,  Cao Zhanyuan (Engineering Technol. Res. Center of Titanium Products and Application of Yunnan Province, Yunnan Titanium Ind. Co. ...) ,  Shi Yaming (Engineering Technol. Res. Center of Titanium Products and Application of Yunnan Province, Yunnan Titanium Ind. Co. ...) ,  Zhang Yuqin (School of Materials Sci. and Engineering, Kunming Univ. of Sci. and Technol., Engineering Technol. Res. Center of ...) ,  Jiang Yehua (School of Materials Sci. and Engineering, Kunming Univ. of Sci. and Technol., Kunming) ,  Zhou Rong (School of Materials Sci. and Engineering, Kunming Univ. of Sci. and Technol., Kunming)
資料名： Zhongguo Youse Jinshu Xuebao  (Zhongguo Youse Jinshu Xuebao)
巻： 25  号： 9  ページ： 2396-2402  発行年： 2015年 
JST資料番号： W0943A  ISSN： 1004-0609  CODEN： ZYJXFK  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： Ti-6Al-4V合金(d10mm)の小寸法棒は高速圧延で作製した。合金棒のミクロ組織と機械的性質に及ぼす溶体化および時効熱処理の影響を調べた。その結果,合金はα相とβ相から成ることを示した。900°Cから990°Cに増加する温度では,一次α相の含有量が減少し,β相の量は増加し,微細構造変換手順は針状変態β相が初晶等軸α相を有し,次に完全なラメラ転移β相への合金で観察された。さらに,合金の引張強度は徐々に上昇し,伸びは顕著に減少した。合金は930°Cの溶液温度で処理し,450°Cから650°Cまでの温度で時効した場合,変態したβ相はα相が析出すると,合金のミクロ組織は(α+β)相とβ相で構成された。一方,α相が成長すると,ミクロ組織は粗くなる。さらに,合金の引張強さは減少し,伸びは増加した。その結果,(930°Cで30分,WQ)+(550 °C, 4 h, AC)の熱処理後に,この合金は最適の機械的性質を,引張強度は1031MPaであり,伸びは12.5%であった。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： 機械的性質 ,  引張強さ ,  β相 ,  溶体化処理 ,  伸び ,  微細構造 ,  *熱処理 ,  ラメラ ,  時効 ,  *チタン ,  金属組織 ,  感情転移 ,  α相 ,  *合金
準シソーラス用語： 初晶 , 【Automatic Indexing@JST】

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (4件)： 高速圧延 ,  Ti-6Al-4V合金 ,  棒 ,  熱処理プロセス