複合核形成剤の最適化およびCaO MgO Al_2O_3SiO_2ガラスセラミックの構造と性質に及ぼす影響【Powered by NICT】

Optimization of Composite Nucleating Agents and Effects on Structure and Properties of CaO-MgO-Al_2O_3-SiO_2 Glass Ceramics

著者 (6件)： Zhang Xuefeng (Key Lab. of Integrated Exploitation of Bayan Obo Multi-Metal Resources,Inner Mongolia Univ. of Sci. and Technol., Baotou) ,  Wei Haiyan (Key Lab. of Integrated Exploitation of Bayan Obo Multi-Metal Resources,Inner Mongolia Univ. of Sci. and Technol., Baotou) ,  Ouyang Shunli (Key Lab. of Integrated Exploitation of Bayan Obo Multi-Metal Resources,Inner Mongolia Univ. of Sci. and Technol., Baotou) ,  Jia Xiaolin (Coll. of Materials Sci. and Engineering, Zhengzhou) ,  Zhao Ming (Key Lab. of Integrated Exploitation of Bayan Obo Multi-Metal Resources,Inner Mongolia Univ. of Sci. and Technol., Baotou) ,  Xia Jingtian (Key Lab. of Integrated Exploitation of Bayan Obo Multi-Metal Resources,Inner Mongolia Univ. of Sci. and Technol., Baotou)
資料名： Rengong Jingti Xuebao  (Rengong Jingti Xuebao)
巻： 44  号： 7  ページ： 1905-1911  発行年： 2015年 
JST資料番号： W0398A  ISSN： 1000-985X  CODEN： RJXUEN  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： Cr_2O_3,Fe_2O_3とCaF_2の余分な添加CaO・MgO al_2o_3sio_2ガラスセラミックは,従来の溶解鋳造法によって調製し,主な材料として化学試薬CaO,MgO,Al_2O_3とSiO_2を用いた。CMASガラスセラミックの複合核形成剤の最適比率を直交試験法により測定した。CaO・MgO Al_2O_3SiO_2ガラスセラミックの微細構造と性質に及ぼす複合核形成剤の効果を,XRD,SEMおよび万能試験機などで調べた。結果は,ガラスセラミックスの曲げ強さはCr_2O_3,Fe_2O_3とCaF_2含量は0.5%,10%,及び8%であるとき,最良であることを示した。複合核形成剤の全含有量が増加するに従って,ガラス系は,より微細な平均粒径を示した。著者らのデータは,細粒ガラスセラミックは良好な硬さを持つことを示した。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： *ガラス ,  鋳造 ,  X線回折 ,  *酸化マグネシウム ,  直交性 ,  試験装置 ,  *ガラスセラミック ,  硬度 ,  曲げ強さ ,  溶解 ,  微細構造 ,  *最適化
準シソーラス用語： 試験方法 , 【Automatic Indexing@JST】

分類 (2件)： 酸化物薄膜  (BK14050P) ,  半導体の結晶成長  (BK13040X)

タイトルに関連する用語 (6件)： 複合核 ,  最適化 ,  CaO ,  MgO ,  ガラスセラミック ,  性質