H_2S/CO_2環境におけるT95鋼の腐食挙動に及ぼす温度の影響を研究した。【JST・京大機械翻訳】

Effect of Temperature on Corrosion Behavior of T95 Steel in H_2S/CO_2 Environment

著者 (7件)： Zeng Dezhi (State Key Laboratory of Oil &Gas Reservoir Geology and Exploitation,Southwest Petroleum University) ,  Deng Wenliang (China Petroleum Pipeline Bureau No.4 Company) ,  Tian Gang (Engineering Technology Research Institute of Xinjiang Oilfield Company) ,  Wang Zhe (State Key Laboratory of Oil &Gas Reservoir Geology and Exploitation,Southwest Petroleum University) ,  Chen Wen (Research Institute of Natural Gas Technology,Petro China Southwest Oil &Gas Field Company) ,  Wang Feng (Research Institute of Natural Gas Technology,Petro China Southwest Oil &Gas Field Company) ,  Hu Junying (State Key Laboratory of Oil &Gas Reservoir Geology and Exploitation,Southwest Petroleum University)
資料名： Jixie Gongcheng Cailiao  (Jixie Gongcheng Cailiao)
巻： 40  号： 6  ページ： 28-32,73  発行年： 2016年 
JST資料番号： C2051A  ISSN： 1000-3738  CODEN： JGCAEL  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 自作の高温オートクレーブを用いて,H_2S/CO_2環境をシミュレーションし,温度30~150°C,H_2S/CO_2気相および模擬地層水相中でT95鋼の腐食試験を行い,腐食速度に及ぼす温度の影響を研究した。腐食生成物の形態と相組成を分析した。結果は以下を示す。温度が30~120°Cの時、T95鋼の気相と液相中の腐食速度はいずれも温度の上昇とともに増加し、90°Cでピーク値に達し、それぞれ0.882、1.096MM・A~(-1)、温度が120°Cより高かった。液相中の腐食速度はゆっくり増加し、気相中のゆっくり減少した。温度の上昇に伴い、気相中の腐食生成物は次第に板状から塊状になり、堆積し、液相中では状状堆積から団塊状になる。腐食生成物は鉄、硫黄、酸素などの元素からなり、腐食速度は腐食生成物の炭素含有量に反比例し、酸素含有量と正比例し、硫黄化合物は腐食に対して阻害作用がある。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 腐食生成物 ,  団塊 ,  地層水 ,  相組成 ,  高温 ,  鉄 ,  液相 ,  オートクレーブ ,  硫黄 ,  腐食速度 ,  *鋼 ,  ピーク値 ,  気相 ,  酸素
準シソーラス用語： *腐食挙動 , 【Automatic Indexing@JST】

著者キーワード (5件)： H_2S/CO_2 environment ,  T95steel ,  temperature ,  corrosion rate ,  corrosion product film

分類 (2件)： 腐食  (WB03030B) ,  腐食基礎理論,腐食試験  (WB03020Q)

タイトルに関連する用語 (3件)： 環境 ,  腐食挙動 ,  研究