Comparison of size dependent strengthening mechanisms in Ag/Fe and Ag/Ni multilayers

著者 (7件)： Li Jin (Department of Materials Science and Engineering, Texas A&M University, College Station, TX 77843-3123, USA) ,  Chen Y. (MPA-CINT, Los Alamos National Laboratory, Los Alamos, NM 87545, USA) ,  Xue S. (Department of Mechanical Engineering, Texas A&M University, College Station, TX 77843-3123, USA) ,  Wang H. (Department of Electrical and Computer Engineering, Texas A&M University, College Station, TX 77843-3128, USA) ,  Zhang X. (Department of Materials Science and Engineering, Texas A&M University, College Station, TX 77843-3123, USA) ,  Zhang X. (Department of Mechanical Engineering, Texas A&M University, College Station, TX 77843-3123, USA) ,  Zhang X. (School of Materials Engineering, Purdue University, West Lafayette, IN 47907, USA)
資料名： Acta Materialia  (Acta Materialia)
巻： 114  ページ： 154-163  発行年： 2016年08月01日 
JST資料番号： A0316A  ISSN： 1359-6454  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ナノ構造化した金属多層膜は,それらがしばしば高い機械的強度を持つためにかなりの注目されている。ここでは,本著者は,各層の厚さ(h)を1nmから200nmまで変化させたスパッタAg/Fe多層膜の微細構造および機械的強度を報告している。体心立方晶(bcc)から面心立方晶(fcc)構造へのFeの相変態はh<5nmの時に起る。ナノ双晶が微細なAg/Fe多層膜において生成する。弾性率ミスマッチはAg/Fe多層膜とAg/Ni多層膜の間で類似しているけれども,Ag/Fe多層膜のピーク硬度はAg/Ni多層膜のピーク硬度よりもかなり低い。いくつかのAgベースの多層膜の機械的強度の比較から,この顕著な違いは層成分の積層欠陥エネルギーの差異による化学的応力から生ずるらしいことが明らかになった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.

シソーラス用語： *銀 ,  *鉄 ,  *ニッケル ,  多層 ,  *多層膜 ,  依存性 ,  強化 ,  機構 ,  金属薄膜 ,  ナノ構造 ,  *機械的強度 ,  微細構造 ,  BCC金属 ,  FCC金属 ,  相変態 ,  膜厚 ,  スパッタ蒸着 ,  蒸着膜 ,  弾性係数 ,  押込硬さ ,  積層欠陥エネルギー ,  ナノインデンテーション
準シソーラス用語： *サイズ依存性

著者キーワード (5件)： Sputter ,  Multilayer ,  Strengthening ,  Nanoindentation ,  Stacking fault energy