Structural Characteristics and Mechanical Behavior of Selective Laser Sintered Porous Ti-6Mo Alloy for Biomedical Applications

著者 (6件)： Xie Fangxia (Jiangsu Key Laboratory of Advanced Food Manufacturing Equipment and Technology, Jiangnan University) ,  He Xueming (Jiangsu Key Laboratory of Advanced Food Manufacturing Equipment and Technology, Jiangnan University) ,  Yu Jinghu (Jiangsu Key Laboratory of Advanced Food Manufacturing Equipment and Technology, Jiangnan University) ,  Wu Meiping (Jiangsu Key Laboratory of Advanced Food Manufacturing Equipment and Technology, Jiangnan University) ,  He Xinbo (University of Science and Technology Beijing) ,  Qu Xuanhui (University of Science and Technology Beijing)
資料名： Xiyou Jinshu Cailiao yu Gongcheng  (Xiyou Jinshu Cailiao yu Gongcheng)
巻： 45  号： 6  ページ： 1477-1482  発行年： 2016年 
JST資料番号： W0563A  ISSN： 1002-185X  CODEN： XJCGEA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 多孔性TI-6MO合金を選択的レーザ焼結によって調製し,多孔性TI-6MO合金を調製し,その構造特性と機械的性質を研究した。結果によると、多孔性TI-6MO合金の孔構造は焼結技術と関係があり、焼結温度が1000°Cから1200°Cに上昇するにつれ、孔隙は三次元連結孔から相互孤立孔になり、多孔度は58%から24%に低下し、孔径は112ΜMから43ΜMに減少した。多孔性TI-6MO合金は室温でラメラ組織であり、いずれも大量のΑ相と少数のΒ相から構成され、微量のΑ析出物を伴う。圧縮応力-歪曲線は弾性変形、塑性降伏と塑性変形段階を示し、多孔度の低下に伴い、弾性係数と降伏強度はそれぞれ2.07~11.9GPAと31.4~152.8MPAに増大した。相対弾性率と相対降伏強さと相対密度の間にはべき乗則関係がある。多孔性TI-6MO合金の空隙特性と機械的性質はいずれも自然骨の要求を満たし、一種の実行可能な医用材料である。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 相対密度 ,  塑性変形 ,  空隙率 ,  弾性変形 ,  *焼結 ,  *多孔性 ,  層状組織 ,  *構造特性 ,  塑性 ,  *合金 ,  降伏強さ ,  降伏 ,  三次元 ,  *付加製造
準シソーラス用語： べき乗則 ,  *選択的レーザ焼結 , 【Automatic Indexing@JST】

著者キーワード (5件)： titanium alloy ,  selective laser sintering ,  porous structure ,  microstructure ,  mechanical properties

分類 (2件)： 医用素材  (GA05040H) ,  圧粉,焼結  (WC02030X)

タイトルに関連する用語 (5件)： 生物医学 ,  多孔性 ,  選択的レーザ焼結 ,  構造特性 ,  機械的挙動