硬質弾性HDPEの微細構造の変化について検討した。【JST・京大機械翻訳】

Change in microstructures of hard elastic HDPE cast film during cold-stretching process

著者 (5件)： Shen Peng (Jiansu Key Laboratory for Sollar Cell Materials & Technology, School of Materials Science & Engineering, Changzhou University) ,  Li Juan (Jiansu Key Laboratory for Sollar Cell Materials & Technology, School of Materials Science & Engineering, Changzhou University) ,  Yang Xingcheng (Jiansu Key Laboratory for Sollar Cell Materials & Technology, School of Materials Science & Engineering, Changzhou University) ,  Liu Jingru (Jiansu Key Laboratory for Sollar Cell Materials & Technology, School of Materials Science & Engineering, Changzhou University) ,  Yu Qiang (Jiansu Key Laboratory for Sollar Cell Materials & Technology, School of Materials Science & Engineering, Changzhou University)
資料名： Huagong Xuebao  (Huagong Xuebao)
巻： 67  号： 7  ページ： 3063-3070  発行年： 2016年 
JST資料番号： E0215B  ISSN： 0438-1157  CODEN： HUKHAI  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 異なる弾性率と引張速度を用いて,室温での硬質弾性HDPEの引張強さを,原子間力顕微鏡,電界放出走査型電子顕微鏡,X線回折,多孔性測定,および透過型電子顕微鏡によって観察した。さらに,微細構造と微細構造に及ぼすこれらの微細構造変化の影響を研究した。研究により、SWRHの倍率を高めることによって、引張の分離程度を増加させ、高い空隙率と多孔性を有する多孔性膜を形成することができるが、SWRHの倍率が高すぎるとラメラの曲げが崩壊し、一部のミクロ孔が閉鎖することが分かった。延伸速度が増加すると,延伸膜中のラメラの分離がより徹底的になり,微細孔の数が増加し,分布がより均一になった。延伸過程における引張応力下での結晶の長い接着力と応力作用下で破壊されたラメラ状エッジの微次晶は,延伸フィルム中の分離ラメラ間の初始橋構造を構成した。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： *弾性 ,  透過型電子顕微鏡 ,  歪速度 ,  走査電子顕微鏡 ,  *高密度ポリエチレン ,  引張 ,  引張強さ ,  引張応力 ,  *微細構造 ,  空隙率 ,  原子間力顕微鏡 ,  *硬質 ,  付着力 ,  多孔性 ,  延伸

著者キーワード (7件)： microporous membrane ,  polymer processing ,  high density polyethylene ,  casting ,  cold-stretching ,  microstructure ,  morphology

分類 (3件)： 酸化物薄膜  (BK14050P) ,  多糖類  (CF10054P) ,  半導体のルミネセンス  (BM08092S)

タイトルに関連する用語 (4件)： 硬質 ,  弾性 ,  HDPE ,  微細構造