熱処理したMG-5GD-3Y-0.5ZR合金のミクロ組織と性質の影響【JST・京大機械翻訳】

Effect of heat treatment on microstructure and properties of Mg-5Gd-3Y-0.5Zr alloy

著者 (5件)： Chen Leilei (School of Materials Science and Engineering,Henan University of Science and Technology) ,  Li Quanan (School of Materials Science and Engineering,Henan University of Science and Technology, Collaborative Innovation Center of Nonferrous Metals) ,  Zhang Xingyuan (School of Materials Science and Engineering,Henan University of Science and Technology; Collaborative Innovation Center of Nonferrous Metals) ,  Chen Jun (School of Materials Science and Engineering,Henan University of Science and Technology; Collaborative Innovation Center of Nonferrous Metals) ,  Zhang Qing (School of Materials Science and Engineering,Henan University of Science and Technology; Collaborative Innovation Center of Nonferrous Metals)
資料名： Cailiao Rechuli Xuebao  (Cailiao Rechuli Xuebao)
巻： 37  号： 2  ページ： 47-51  発行年： 2016年 
JST資料番号： C2127A  ISSN： 1009-6264  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： XRD、OM、SEM、EDS、TEMと引張性能試験を用いて,異なる熱処理したMG-5GD-3Y-0.5Z合金の組織と機械的性質の影響を研究した。結果:MG-5GD-3Y-0.5ZR合金の鋳放し組織は主にマトリックス相からΑ-MG_MG_5GDとMG_(24)Y_5相組成;溶液処理後,鋳放し組織中の粗大析出相はすべてはΑ-MGマトリックス溶け基本;再時効処理を経た後に,ナノレベルの粒状或片状相再析出がある。室温条件下では,MG-GD-3Y-0.5ZR合金の引張強度はT6状態では最大値に達すると206.6MPA5。鋳放しとT6状態の合金の引張強度は,いずれも温度の上昇とともに,減少傾向を示し,しかも低下速度は速く;にT4状態での合金の強度は250°C以前ではほぼ一定に保たれる。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 相組成 ,  性能試験 ,  機械的性質 ,  フレーク ,  *合金 ,  鋳放し ,  引張強さ ,  引張
準シソーラス用語： 溶液処理 , 【Automatic Indexing@JST】

著者キーワード (3件)： Mg-5Gd-3Y-0.5Zr alloy ,  microstructure ,  mechanical property

分類 (1件)： 変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (3件)： 熱処理 ,  ミクロ組織 ,  性質