パルス爆発-プラズマ処理はM42高速度鋼の表面を修飾した。【JST・京大機械翻訳】

Surface modification of M42 high speed steel by pulse detonation-plasma treatment

著者 (8件)： Liao Xianjin (Jiangxi Key Laboratory of Advanced Copper and Tungsten Materials,Jiangxi Academy of Sciences) ,  Lu Lei (Jiangxi Key Laboratory of Advanced Copper and Tungsten Materials,Jiangxi Academy of Sciences) ,  Fu Qingfeng (Jiangxi Key Laboratory of Advanced Copper and Tungsten Materials,Jiangxi Academy of Sciences) ,  Zhou Zhe (Jiangxi Key Laboratory of Advanced Copper and Tungsten Materials,Jiangxi Academy of Sciences) ,  Yu Jiumin (Jiangxi Key Laboratory of Advanced Copper and Tungsten Materials,Jiangxi Academy of Sciences) ,  Zou Jin (Jiangxi Key Laboratory of Advanced Copper and Tungsten Materials,Jiangxi Academy of Sciences) ,  Zhang Linwei (Jiangxi Key Laboratory of Advanced Copper and Tungsten Materials,Jiangxi Academy of Sciences) ,  Lu Deping (Jiangxi Key Laboratory of Advanced Copper and Tungsten Materials,Jiangxi Academy of Sciences)
資料名： Jinshu Rechuli  (Jinshu Rechuli)
巻： 40  号： 12  ページ： 166-170  発行年： 2015年 
JST資料番号： C2061A  ISSN： 0254-6051  CODEN： JRECDB  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： M42高速度鋼の表面硬度と耐摩耗性を向上のため,-爆発パルス等を利用してプラズマ(PDP)では,この鋼の表面を改質を行う。SEM、XRDにより、微小硬さ、摩擦摩耗試験機,パルス処理前後の表面形態、元素組成、表面硬度と耐摩耗性の変化を研究した。結果は表層のマルテンサイト(Α-FE)オーステナイト(Γ-FE)への転移,Γ-FE中に少量の炭化物FEW_3C溶解し,表層残留応力そして結晶粒微細化圧が出現し,WとOなどの元素からなる表面の「雨滴」状熔滴で堆積したことを示唆する。2回のパルス処理を経た後,硬化層は最も厚く,耐摩耗性は良好であった。Data from the ScienceChina, LCAS.【JST・京大機械翻訳】

シソーラス用語： 耐摩耗性 ,  炭化物 ,  微小硬さ ,  *プラズマ処理 ,  液滴 ,  表層 ,  *高速度鋼 ,  残留応力 ,  硬化層 ,  オーステナイト ,  X線回折 ,  *パルス ,  結晶粒微細化
準シソーラス用語： 表面形態 ,  表面硬度 , 【Automatic Indexing@JST】

著者キーワード (4件)： pulse detonation-plasma treatment ,  M42 high speed steel ,  surface modification ,  wear resistance

分類 (3件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U) ,  金属の機械的性質  (BL01022T)

タイトルに関連する用語 (5件)： パルス ,  爆発 ,  プラズマ処理 ,  高速度鋼 ,  修飾