550°Cでの酸素飽和停滞した鉛-ビスマス共晶における高Siフェライト/マルテンサイト鋼の耐酸化性に及ぼす予変形の影響【Powered by NICT】

Effect of pre-deformation on the oxidation resistance of a high Si ferritic/martensitic steel in oxygen-saturated stagnant lead-bismuth eutectic at 550°C

著者 (4件)： Dong Hong (Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences,72 Wenhua Road, Shenyang 110016, China) ,  Wang Pei (Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences,72 Wenhua Road, Shenyang 110016, China) ,  Li Dianzhong (Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences,72 Wenhua Road, Shenyang 110016, China) ,  Li Yiyi (Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences,72 Wenhua Road, Shenyang 110016, China)
資料名： Corrosion Science  (Corrosion Science)
巻： 118  ページ： 129-142  発行年： 2017年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： と550°Cで酸素飽和停滞した鉛-ビスマス共晶における予備変形無し高Siフェライト/マルテンサイト鋼の耐酸化性を調べた。予変形は酸化物スケールの形態を局所的に変化させることが分かった。いくつかの位置では,内部酸化物層下に内部酸化の領域は消失しおよび/または内部酸化物層の厚さは減少した。これらの変化は,内部酸化物層中の局所的に増強されたCrリッチ帯の形成に関係している。さらに,局所強化されたCrリッチ帯は内部/外部酸化物層界面,材料の耐酸化性を劣化させるで多くのボイドを誘導する。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *耐酸化性 ,  界面 ,  *共晶 ,  酸化物 ,  *鋼 ,  *フェライト ,  *酸化 ,  *マルテンサイト鋼 ,  内部酸化
準シソーラス用語： 酸化物層 , 【Automatic Indexing@JST】

著者キーワード (5件)： A鋼 ,  B SEM ,  B STEM ,  C.効果ひずみ ,  C酸化

分類 (1件)： 腐食  (WB03030B)

タイトルに関連する用語 (8件)： 酸素 ,  飽和 ,  停滞 ,  鉛-ビスマス共晶 ,  Si ,  フェライト ,  マルテンサイト鋼 ,  耐酸化性