J-GLOBAL ID：201702213484322287   整理番号：17A0067408

Lin聚芳MiTong粒子を含有する層間増繊維/ビスマレイミド樹脂複合材料を調製した。【JST・京大機械翻訳】

Properties of Interlaminar Toughened CF/BMI Composites by Phosphorus-Containing PAEK Particles

著者 (7件)： Zhang Xingdi (Alan G. MacDiarmid Institute,College of Chemistry,Jilin University) ,  Liu Gang (Key Laboratory of Advanced Composites,Beijing Institute of Aeronautical Materials,AVIC Composites Center) ,  Dang Guodong (Alan G. MacDiarmid Institute,College of Chemistry,Jilin University) ,  Zhang Jindong (Key Laboratory of Advanced Composites,Beijing Institute of Aeronautical Materials,AVIC Composites Center) ,  Zhou Hongwei (Alan G. MacDiarmid Institute,College of Chemistry,Jilin University) ,  Chen Chunhai (Alan G. MacDiarmid Institute,College of Chemistry,Jilin University) ,  Bao Jianwen (Key Laboratory of Advanced Composites,Beijing Institute of Aeronautical Materials,AVIC Composites Center)
資料名： Gaofenzi Xuebao  (Gaofenzi Xuebao)
号： 9  ページ： 1254-1262  発行年： 2016年 
JST資料番号： W0847A  ISSN： 1000-3304  CODEN： GAXUE9  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 強化剤としてのビスマレイミド樹脂(BMI)を用いて,溶解(P-PAEK)の熱可塑性樹脂を強化剤として用いて,層繊維強化ビスマレイミド樹脂複合材料を調製した。異なる樹脂含有量が樹脂の鋳造特性に及ぼす影響を研究し、走査型電子顕微鏡を用いて複合系のミクロ形態を分析し、その強靭化メカニズムを分析し、層間破壊靭性試験により、ビスマレイミド樹脂複合材料の強靭化前後の層間靱性性能を特性化した。結果は,複合材料のI型層間破壊靱性(G_(IC))が0.54KJ/M2であり,II型層間破壊靭性(G_(IIC))が1.36KJ/M2であることを示した。それらは,複合材料と比較して,それぞれ56%と42%増加した。複合材料は,従来の機械的性質を維持するとともに,衝撃強さ(CAI)は約29%増加し,層間せん断強さは111.7MPAに達した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *複合材料 ,  鋳造 ,  破壊靱性試験 ,  熱可塑性プラスチック ,  破壊靱性 ,  走査電子顕微鏡 ,  靱性 ,  繊維強化 ,  複合系 ,  *コンポジットレジン ,  キャラクタリゼーション ,  衝撃強さ ,  *歯科用材料
準シソーラス用語： 層間剪断強さ ,  強靱化 ,  *ビスマレイミド , 【Automatic Indexing@JST】

著者キーワード (4件)： P-PAEK ,  BMI ,  Toughened ,  Composites

分類 (2件)： 機械的性質  (YH02022L) ,  ゴム・プラスチック材料試験  (HB03000F)

タイトルに関連する用語 (4件)： 繊維 ,  ビスマレイミド ,  樹脂複合材料 ,  調製