多結晶Co-Ni基超合金の酸化機構に及ぼす合金化効果【Powered by NICT】

Alloying effects on oxidation mechanisms in polycrystalline Co-Ni base superalloys

著者 (6件)： Ismail F.B. (Department of Materials, Royal School of Mines, Imperial College, Prince Consort Road, South Kensington, London SW7 2BP, UK) ,  Vorontsov V.A. (Department of Materials, Royal School of Mines, Imperial College, Prince Consort Road, South Kensington, London SW7 2BP, UK) ,  Lindley T.C. (Department of Materials, Royal School of Mines, Imperial College, Prince Consort Road, South Kensington, London SW7 2BP, UK) ,  Hardy M.C. (Rolls-Royce plc, ELT-10, PO Box 31, Derby DE24 8BJ, UK) ,  Dye D. (Department of Materials, Royal School of Mines, Imperial College, Prince Consort Road, South Kensington, London SW7 2BP, UK) ,  Shollock B.A. (WMG, University of Warwick, Coventry CV4 7AL, UK)
資料名： Corrosion Science  (Corrosion Science)
巻： 116  ページ： 44-52  発行年： 2017年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 多結晶Co-Ni-Cr-Al W Ta合金の酸化機構は,集束イオンビーム二次イオン質量分析計(FIB SIMS)におけるO16十八同位体トレーサ分析を用いて調べた。Al添加は連続アルミナリッチ層の形成に有利であることを,Crは耐酸化性を改善した間接的とCo分率の増加不良酸化性能をもたらすことが分かった。at.%Al at.%Crと1015を含む合金では,800°Cで200hの酸化後に形成された外側スケールは厚さ1μm以下の酸化物から構成された。保護酸化物スケールはCo-Ni基超合金に形成されることができると結論される。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *合金 ,  耐酸化性 ,  *超合金 ,  集束イオンビーム ,  *酸化 ,  アルミニウム ,  酸化物 ,  *合金化 ,  クロム ,  *多結晶
準シソーラス用語： *酸化機構 , 【Automatic Indexing@JST】