弾性シリコーンゴム被覆の調製と耐摩耗性の研究【JST・京大機械翻訳】

Preparation and anti-icing properties of flexible addition-cured silicone rubber coating

著者 (5件)： Guan Dongbo (College of Materials Science and Engineering, Key Laboratory of Automobile Materials of Ministry of Education, Jilin University) ,  Cai Zhongyi (Jilin University Roll Forging Technology Research Institute) ,  Zhang Jitang (College of Materials Science and Engineering, Key Laboratory of Automobile Materials of Ministry of Education, Jilin University) ,  Qiu Xiaoming (College of Materials Science and Engineering, Key Laboratory of Automobile Materials of Ministry of Education, Jilin University) ,  Dou Yanli (College of Materials Science and Engineering, Key Laboratory of Automobile Materials of Ministry of Education, Jilin University)
資料名： Gongneng Cailiao  (Gongneng Cailiao)
巻： 47  号： 8  ページ： 8008-8012  発行年： 2016年 
JST資料番号： C2095A  ISSN： 1001-9731  CODEN： GOCAEA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 4種類のコーティングに対して、接線着氷サイクル剥離試験を行った結果、サンプルAコーティングは高い接触角を有するが、接線の剥離回数が増加するにつれ、コーティングの接触角が次第に低下し、方向の接着強度が次第に増大することが分かった。しかし,B,C,Dコーティングの表面接触角と引張強さはほとんど変化しないが,Bのコーティング層の接着強さは低く,B含有量が20%のときには,異なる含有量の端を添加することにより,それらの質量分率は20%であった。コーティングは,より高い接触角とより低い接着強さを持ち,最終的に,エンドの質量分率が20%のときに,異なる着氷温度と着氷時間による方向の接着強さの試験結果は,粘着時間の延長と粘着の温度の低下によることを示した。氷とコーティングの表面の接着強さは徐々に増加する傾向を示し,最後に,より良い除氷時間と温度を与えた。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 接着強さ ,  *ポリシロキサン ,  剥離試験 ,  引張強さ ,  除氷 ,  *被覆 ,  被覆層 ,  *耐摩耗性 ,  接触角 ,  *弾性 ,  着氷
準シソーラス用語： 粘着 ,  質量分率 ,  *ゴム被覆 , 【Automatic Indexing@JST】

著者キーワード (3件)： flexible addition-cured silicone rubber ,  contact angle ,  shear stress of ice detachment