文献

J-GLOBAL ID：201702214051437936   整理番号：17A0103601

種晶促進相転移によるメソ多孔質アルミナ限外ろ過膜の調製【JST・京大機械翻訳】

Fabrication of small pore size alpha alumina ultrafiltration membrane by phase transition with the aid ofα-Al_2O_3 seeds

著者 (5件)： Zhang Wei (State Key Laboratory of Materials-Oriented Chemical Engineering,College of Chemistry and Chemical Engineering,Nanjing Tech University) ,  Chen Xianfu (State Key Laboratory of Materials-Oriented Chemical Engineering,College of Chemistry and Chemical Engineering,Nanjing Tech University) ,  Lin Yuqing (State Key Laboratory of Materials-Oriented Chemical Engineering,College of Chemistry and Chemical Engineering,Nanjing Tech University) ,  Qiu Minghui (State Key Laboratory of Materials-Oriented Chemical Engineering,College of Chemistry and Chemical Engineering,Nanjing Tech University) ,  Fan Yiqun (State Key Laboratory of Materials-Oriented Chemical Engineering,College of Chemistry and Chemical Engineering,Nanjing Tech University)
資料名： Mokexue yu Jishu  (Mokexue yu Jishu)
巻： 36  号： 1  ページ： 12-16,22  発行年： 2016年 
JST資料番号： W1530A  ISSN： 1007-8924  CODEN： MKYJEF  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： ゾル-ゲル法によって調製されたΑ-酸化相に基づいて,Α-相形核后の高温での成長を促進するために,適切な量のアルミナ種を添加することによって,Α相の結晶相変態を促進することができた。さらに,より小さなアルミナ粒子の堆積膜を得て,優れた遮断性能を有する径の限外ろ過膜を調製した。結果は以下を示す。この方法により,6%DWB%(DWB%)の添加により,AL_2O_3結晶は,1000°C,1Hの条件下で完全にΑ相変態を起こすことが分かった。調製したΑ-酸化の除去性能は純ベーマイトにより調製したものよりも大きく,細孔径は小さく,その相対分子量は13であり,対応する細孔径は5.2NMであった。純水の浸透率は1400L/(M2H・MPA)であった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 純水 ,  *アルミナ ,  *種結晶 ,  ベーマイト ,  ゾル-ゲル法 ,  浸透率 ,  結晶 ,  *相転移 ,  細孔径 ,  分子量 ,  高温
準シソーラス用語： 除去性能 ,  遮断 ,  *限外濾過膜 ,  *メソ多孔質アルミナ , 【Automatic Indexing@JST】

著者キーワード (4件)： sol-gel ,  alpha alumina ,  α-Al_2O_3 seeds ,  ultrafiltration membrane

分類 (1件)： 膜分離  (XD02120Z)

タイトルに関連する用語 (6件)： 種晶 ,  促進 ,  相転移 ,  メソ多孔質アルミナ ,  限外ろ過膜 ,  調製