2種類の表面状態のHAYNES 282の750°C高温蒸気中での酸化挙動【JST・京大機械翻訳】

Oxidation Behavior of Haynes 282 With Two Surface Conditions in Steam at 750°C

著者 (4件)： Tang Liying (National Energy R & D Center of Clean and High-Efficiency Fossil-Fired Power Generation Technology, Xi’an Thermal Power Research Institute Co. Ltd.) ,  Zhou Rongcan (National Energy R & D Center of Clean and High-Efficiency Fossil-Fired Power Generation Technology, Xi’an Thermal Power Research Institute Co. Ltd.) ,  Hou Shufang (National Energy R & D Center of Clean and High-Efficiency Fossil-Fired Power Generation Technology, Xi’an Thermal Power Research Institute Co. Ltd.) ,  Wang Bohan (National Energy R & D Center of Clean and High-Efficiency Fossil-Fired Power Generation Technology, Xi’an Thermal Power Research Institute Co. Ltd.)
資料名： Zhongguo Dianji Gongcheng Xuebao  (Zhongguo Dianji Gongcheng Xuebao)
巻： 36  号： 10  ページ： 2728-2733  発行年： 2016年 
JST資料番号： C2285A  ISSN： 0258-8013  CODEN： ZDGXER  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 2種類の表面状態のHAYNES 282合金の750°C高温蒸気中2000時間の酸化挙動を研究した。結果は以下を示す。結果は,表面-Pと保持管の内壁における282-Wの酸化物が,連続的にCR_2O_3+TIO_2+(MN,FE,CR)_3O_4相と結晶粒界に分布するAL_2O_3酸化物から成ることを示した。しかし,282-Pの酸化物のTIO_2含有量は282-Wよりも高く,一方,(MN,FE,CR)_3O_4の含有量は282-Wよりも低かった。282-Wの酸化層のTIO_2は大粒子状態で存在するが、282-Wの酸化層のTIO_2とCR_2O_3は明らかな形態差異がない。282-Pの厚さは282Wよりも大きいが,282-Wの酸化層の厚さと成長速度は282-Pよりもはるかに大きい。合金の抗水蒸気酸化性能は2種類の試料タイプに合わせて総合的に評価する必要がある。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 結晶粒界 ,  酸化層 ,  合金 ,  成長速度 ,  酸化物 ,  *酸化 ,  *高温
準シソーラス用語： *酸化挙動 , 【Automatic Indexing@JST】

著者キーワード (4件)： Haynes 282 ,  steam oxidation ,  surface condition ,  750°C