Preparation and Characterization of Sodium-potassium Bismuth Titanate Lead Free Piezoelectric Thick Films

著者 (4件)： ZHANG Hai-bo (Dept. of Electronic Science and Technology, Engineering Research Centre for Functional Ceramics MOE Huazhong University of Science and Technology) ,  JIANG Sheng-lin (Dept. of Electronic Science and Technology, Engineering Research Centre for Functional Ceramics MOE Huazhong University of Science and Technology) ,  ZENG Yi-ke (Dept. of Electronic Science and Technology, Engineering Research Centre for Functional Ceramics MOE Huazhong University of Science and Technology) ,  ZHANG Yang-yang (Dept. of Electronic Science and Technology, Engineering Research Centre for Functional Ceramics MOE Huazhong University of Science and Technology)
資料名： Yadian yu Shengguang  (Yadian yu Shengguang)
巻： 31  号： 4  ページ： 553-555  発行年： 2009年 
JST資料番号： C2465A  ISSN： 1004-2474  CODEN： YASHE7  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 従来の固相反応法(NA_(0.82)K_(0.18))_(0.5)BI_(0.5)TIO_3無鉛圧電セラミック粉末を用いて,質量分率5%のエチルセルロースを質量分率92%のテルピネオールに添加した。質量分率2%の二酸ナトリウムを分散剤とし、質量分率1%のフタル酸ジブチルを可塑剤とし、セラミック粉末と接着剤溶液を3:3とした。1つの質量比が混合粉砕により、320メッシュの白金電極をPT電極を持つアルミナ基板上に、寝かせたり、乾燥、焼結、加圧及び焼結後、厚さ約40ΜMのBNKT厚膜を作製し、平均粒径は1.1ΜMであり、誘電率も最大となった。最小損失は3.6%(10KHZ)であり,残留分極は24.8ΜC/CM2であり,縦方向の圧電係数は79KV/CMであった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 厚膜 ,  *キャラクタリゼーション ,  焼結 ,  可塑剤 ,  固相反応 ,  誘電率 ,  エチルセルロース ,  セラミック ,  粉体 ,  残留分極 ,  白金電極 ,  分散剤
準シソーラス用語： 圧電定数 ,  質量分率 ,  鉛フリー圧電セラミックス , 【Automatic Indexing@JST】

著者キーワード (5件)： sodium-potassium bismuth titanate ,  piezoelectric thick films ,  screen printing ,  ferroelectric hysteresis ,  longitudinal piezoelectric coefficient

分類 (2件)： セラミック・陶磁器の製造  (YC03020V) ,  圧粉,焼結  (WC02030X)

タイトルに関連する用語 (3件)： 酸 ,  調製 ,  キャラクタリゼーション