Heat Deformation and Heat Treatment Process of Ti-6321 Alloy Bars

著者 (8件)： Chen Haisheng (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University) ,  Luo Jinhua (Western Superconducting Technologies Co., Ltd) ,  Wang Wensheng (Western Superconducting Technologies Co., Ltd) ,  Sun Xiaoping (Western Superconducting Technologies Co., Ltd) ,  Liu Xianghong (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University) ,  Feng Yong (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University) ,  Zhang Pingxiang (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University) ,  Fu Hengzhi (State Key Laboratory of Solidification Processing, Northwestern Polytechnical University)
資料名： Xiyou Jinshu Cailiao yu Gongcheng  (Xiyou Jinshu Cailiao yu Gongcheng)
巻： 45  号： 11  ページ： 2948-2952  発行年： 2016年 
JST資料番号： W0563A  ISSN： 1002-185X  CODEN： XJCGEA  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： TI-TI/TI合金の相変態領域を加熱領域で加熱し,50%~80%の冷間変形と通常の焼なましを行った後に,微細構造の変化は見られなかったが,Α相の微細構造は明らかに改善された。変形量が増加するにつれて,結晶粒微細化の程度は増加し,ロッドの強度は増加傾向を示し,衝撃靭性は減少した。Φ45MM規格棒に対して,通常焼鈍,二重アニーリング,Β焼鈍および溶体化時効熱処理を行った。結果は,TI-6321鋼の微細構造と性質が熱処理工程に敏感で,環境の具体的要求に従って適切な熱処理技術を選択し,最終的に材料強度,塑性と靱性の良好なマッチングを実現することを示した。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 時効 ,  *熱処理 ,  靱性 ,  鋼 ,  焼なまし ,  規格 ,  微細構造 ,  溶体化処理 ,  *合金 ,  塑性 ,  結晶粒微細化
準シソーラス用語： 材料強度 ,  衝撃靱性 , 【Automatic Indexing@JST】

著者キーワード (5件)： Ti-6321 titanium alloy ,  deformation ,  heat treatment ,  microstructure ,  property

分類 (1件)： 機械的性質  (WB02030U)

タイトルに関連する用語 (2件)： Ti合金 ,  熱処理