押出状態での96の結晶粒の異常成長に及ぼす変形温度と変形の影響を研究した。【JST・京大機械翻訳】

Effect of Deforming Temperature and Strain on Abnormal Grain Growth of Extruded FGH96 Superalloy

著者 (7件)： Wang Chaoyuan (Laboratory of Welding and Plastic Forming,Beijing Institute of Aeronautical Materials) ,  Dong Yunpeng (Laboratory of Welding and Plastic Forming,Beijing Institute of Aeronautical Materials) ,  Song Xiaojun (Laboratory of Welding and Plastic Forming,Beijing Institute of Aeronautical Materials) ,  Fang Shuang (Laboratory of Welding and Plastic Forming,Beijing Institute of Aeronautical Materials) ,  Yu Qiuying (Laboratory of Welding and Plastic Forming,Beijing Institute of Aeronautical Materials) ,  Li Kai (Laboratory of Welding and Plastic Forming,Beijing Institute of Aeronautical Materials) ,  Wang Shuyun (Laboratory of Welding and Plastic Forming,Beijing Institute of Aeronautical Materials)
資料名： Hangkong Cailiao Xuebao  (Hangkong Cailiao Xuebao)
巻： 36  号： 5  ページ： 14-20  発行年： 2016年 
JST資料番号： C2691A  ISSN： 1005-5053  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 楔形試料の等温鍛造試験に基づき,DEFORM-3Dシミュレーションソフトウェアを用いて,異なる位置の変形を測定し,異なる変形温度と異なる変形量が押出したFGH96合金の結晶成長に及ぼす影響を研究した。結果は以下を示す。圧力速度は0であった。04MM/Sの平模Dui粗試験条件の下で,押96合金の臨界変形温度は1100°Cであり,臨界変形は2%であった。1000~1070°Cの鍛造変形では,合金の結晶粒の異常な成長が起こり,しかし,臨界変形の特性があり,5%~10%の変形領域での平均粒径は最大であった。15%以上の変形量を選択することによって,結晶粒の異常成長を避けることができ,均一な微細構造を得ることができた。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 等温鍛造 ,  結晶成長 ,  *成長異常 ,  微細構造 ,  三次元 ,  臨界 ,  鍛造 ,  楔形 ,  合金 ,  *結晶粒
準シソーラス用語： シミュレーションソフトウェア ,  *変形温度 , 【Automatic Indexing@JST】

著者キーワード (5件)： FGH96 superalloy ,  wedge-shaped sample ,  critical deforming temperature ,  critical strain ,  abnormal grain growth

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (5件)： 押出 ,  結晶粒 ,  異常成長 ,  変形温度 ,  研究