ZSM-5/ZSM-11共生ゼオライトを,協同的水素化によって合成した。【JST・京大機械翻訳】

Synthesis of ZSM-5/ZSM-11 Intergrowth Zeolite via the Synergetic Directing Approach

著者 (4件)： Fu Wenhua (State Key Laboratory of Green Chemical Engineering and Industrial Catalysis, Shanghai Research Institute of Petrochemical Technology, SINOPEC) ,  Yuan Zhiqing (State Key Laboratory of Green Chemical Engineering and Industrial Catalysis, Shanghai Research Institute of Petrochemical Technology, SINOPEC) ,  Wang Yangdong (State Key Laboratory of Green Chemical Engineering and Industrial Catalysis, Shanghai Research Institute of Petrochemical Technology, SINOPEC) ,  Yang Weimin (State Key Laboratory of Green Chemical Engineering and Industrial Catalysis, Shanghai Research Institute of Petrochemical Technology, SINOPEC)
資料名： Huaxue Fanying Gongcheng yu Gongyi  (Huaxue Fanying Gongcheng yu Gongyi)
巻： 32  号： 5  ページ： 400-407  発行年： 2016年 
JST資料番号： C2009A  ISSN： 1001-7631  CODEN： HFGGEU  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： ZSM-5/ZSM-11共生ゼオライトを,4-テトラブチルアンモニウム(TBA+)テンプレートと,ゼオライト分子ふるいを用いて合成した。BETAゼオライト種の添加はZSM-5/ZSM-11ゼオライトの合成相を拡大し,モルデナイト相の生成を抑制した。ZSM-5,ZSM-11の含有量およびゼオライト結晶形態に及ぼす合成条件の影響を研究し,そして,同じ条件下で,結晶粒のサイズが,より大きいほど,結晶粒度は,より高く,そして,複合材料中のZSM-11の含有量は,より高かった。X線回折(XRD)、走査型電子顕微鏡(SEM)、N_2物理吸着(BET)、(27)ALマジック角スピニング固体NMR(MAS-NMR)、NH_3昇温脱着(NH_3-TPD)などによってサンプルを特性化した。ZSM-5/ZSM-11共生ゼオライトは高い結晶度,豊富な孔構造,優れたALの配位状態と強酸性を有し,潜在的応用価値を有する優れた触媒であることが分かった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  分子ふるい ,  昇温脱離 ,  結晶粒度 ,  走査電子顕微鏡 ,  モルデナイト ,  キャラクタリゼーション ,  物理吸着 ,  結晶形態 ,  結晶度 ,  *水素化 ,  結晶粒
準シソーラス用語： 強酸 ,  マジック角回転 ,  *ZSM-11 , 【Automatic Indexing@JST】

著者キーワード (4件)： ZSM-5/ZSM-11 intergrowth zeolite ,  synergetic directing ,  tetrabutylammonium ,  Beta seed

分類 (1件)： 粉末製造  (WC02020M)

タイトルに関連する用語 (4件)： 共生 ,  ゼオライト ,  協同 ,  水素化