J-GLOBAL ID：201702224131604299   整理番号：17A0445820

スパークプラズマ焼結により調製した近傍及びサブミクロン粒径の銅の微細構造と機械的強度【Powered by NICT】

Microstructure and mechanical strength of near- and sub-micrometre grain size copper prepared by spark plasma sintering

著者 (4件)： Zhu K.N. (Key Laboratory of Advanced Materials (MOE), School of Materials Science and Engineering, Tsinghua University, Beijing 100084, China) ,  Godfrey A. (Key Laboratory of Advanced Materials (MOE), School of Materials Science and Engineering, Tsinghua University, Beijing 100084, China) ,  Hansen N. (Section for Materials Science and Advanced Characterization, Department of Wind Energy, Technical University of Denmark, Riso Campus, 4000 Roskilde, Denmark) ,  Zhang X.D. (Section for Materials Science and Advanced Characterization, Department of Wind Energy, Technical University of Denmark, Riso Campus, 4000 Roskilde, Denmark)
資料名： Materials & Design  (Materials & Design)
巻： 117  ページ： 95-103  発行年： 2017年 
JST資料番号： A0495B  ISSN： 0264-1275  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： スパークプラズマ焼結(SPS)は,近及びサブミクロン級の結晶粒径をもつ完全に再結晶化した条件における銅の完全に緻密な試料を作製した。二合成ルートは,粒径制御を達成するために調査した(i)800~1000°Cの種々の温度でSPS,と(ii)800°CでSPSの後の温度でのアニーリングにより950~1050°Cであった。平均粒径≒0.5μmの初期球状粉末を用いて,0.5から3μmの範囲の平均粒径を持つ試料を調製した。微細構造試験から,透過型電子顕微鏡の両方に,および電子後方散乱回折研究に基づいて,試料はほぼ完全に再結晶した状態にある,無転位,ランダム集合組織を持つことを結晶粒,高傾角粒界の高い割合を確認した。試料の機械的強度を硬度測定と引張試験を用いて調べ,約1μm以下の粒径をもつ試料のための強化された強度を明らかにした。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 焼なまし ,  *粒径 ,  結晶粒径 ,  *銅 ,  再結晶 ,  引張試験 ,  結晶粒 ,  *放電プラズマ焼結 ,  透過型電子顕微鏡 ,  *機械的強度 ,  高傾角粒界
準シソーラス用語： 硬さ測定 ,  EBSD ,  平均粒子径 ,  粒径制御 , 【Automatic Indexing@JST】

著者キーワード (4件)： スパークプラズマ焼結 ,  銅 ,  超微細粒径 ,  機械的性質

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (8件)： スパークプラズマ焼結 ,  調製 ,  近傍 ,  サブ ,  粒径 ,  銅 ,  微細構造 ,  機械的強度