界面析出炭化物強化二相Ti含有鋼の開発に及ぼすCrおよびAl添加の影響【Powered by NICT】

Effect of Cr and Al additions on the development of interphase-precipitated carbides strengthened dual-phase Ti-bearing steels

著者 (6件)： Tsai Shao-Pu (Department of Materials Science and Engineering, National Taiwan University, Taipei, Taiwan) ,  Su Te-Cheng (Department of Materials, Imperial College London, London, United Kingdom) ,  Yang Jer-Ren (Department of Materials Science and Engineering, National Taiwan University, Taipei, Taiwan) ,  Chen Chih-Yuan (Graduate Institute of Intellectual Property, National Taipei University of Technology, Taipei, Taiwan) ,  Wang Yuan-Tsung (Iron and Steel R&D Department, China Steel Corporation, Kaohsiung, Taiwan) ,  Huang Ching-Yuan (Iron and Steel R&D Department, China Steel Corporation, Kaohsiung, Taiwan)
資料名： Materials & Design  (Materials & Design)
巻： 119  ページ： 319-325  発行年： 2017年 
JST資料番号： A0495B  ISSN： 0264-1275  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 機械的性質(655MPaの降伏強さ,911MPaの極限引張強さ,30%の伸び)の優れた組み合わせを有するTi Cr軸受熱間圧延二相鋼の開発を達成した。フェライト中の界面析出ナノメータサイズの炭化物から得られた重要な強化のために,この二相鋼は,降伏比が約0.72で,従来の二相鋼のそれよりもはるかに高い。膨張計に関する等温変態はTi基鋼におけるオーステナイトからフェライトへの変態に及ぼすCrとAl添加の効果を調べた。0.6wt.%Crの添加は明らかにフェライトの変態速度を遅らせることが分かった,0.1wt.%Alの添加と比較した。膨張計と透過型電子顕微鏡からの結果は,Ti Cr軸受鋼のより低い変態速度のために,フェライト中のナノメータサイズ界面析出炭化物の非常に高い密度は650°Cでの等温保持中に起こり,フェライトの強度の著しい増加に導くことを明らかにした。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 二相鋼 ,  *アルミニウム ,  恒温変態 ,  *チタン ,  フェライト ,  オーステナイト ,  *鋼 ,  降伏強さ ,  *界面 ,  熱間圧延 ,  *クロム ,  引張強さ ,  *炭化物
準シソーラス用語： 変態速度 ,  膨張計 , 【Automatic Indexing@JST】

著者キーワード (6件)： 二相鋼 ,  収量比 ,  相間析出したナノメートルサイズの炭化物 ,  膨張計 ,  等温変態 ,  透過型電子顕微鏡観察

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (8件)： 界面 ,  析出 ,  炭化物 ,  強化 ,  Ti ,  開発 ,  Cr ,  Al