Na_1/3Ca_1/3Bi_1/3Cu₃Ti₄O₁₂ナノ粒子によって誘起されるポリ(フッ化ビニリデン)系高分子複合材料における誘電率の大幅な向上

Greatly enhanced dielectric permittivity in poly(vinylidene fluoride)-based polymeric composites induced by Na1/3Ca1/3Bi1/3Cu3Ti4O12 nanoparticles

著者 (4件)： Kum-onsa Pornsawan (Materials Science and Nanotechnology Program, Faculty of Science, Khon Kaen University, Khon Kaen, Thailand) ,  Thongbai Prasit (Integrated Nanotechnology Research Center (INRC), Department of Physics, Faculty of Science, Khon Kaen University, Khon Kaen, Thailand) ,  Maensiri Santi (School of Physics, Institute of Science, Suranaree University of Technology, Nakhon Ratchasima, Thailand) ,  Chindaprasirt Prinya (Sustainable Infrastructure Research and Development Center, Department of Civil Engineering, Faculty of Engineering, Khon Kaen University, Khon Kaen, Thailand)
資料名： Journal of Materials Science. Materials in Electronics  (Journal of Materials Science. Materials in Electronics)
巻： 27  号： 9  ページ： 9650-9655  発行年： 2016年09月 
JST資料番号： W0003A  ISSN： 0957-4522  CODEN： JMTSAS  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： Na_1/3Ca_1/3Bi_1/3Cu₃Ti₄O₁₂(NCB)ナノ粒子を組み込むことによって,ポリ(フッ化ビニリデン)(PVDF)高分子複合材料の誘電率(ε’)が大幅に増加した。NCB/PVDF複合材料を従来の混合粉末及びホットプレスによって作製した。化学燃焼法及び固相反応法によって,それぞれ,調製したナノサイズ(NCB-NP)及びマイクロサイズ粉末(NCB-MP)を充填剤として用いた。PVDFマトリックス中でのNCB-NPの分散は,かなり良好であった。NCB-MP/PVDF複合材料と比較して,NCB-NPによって充填することで,PVDF系高分子複合材料のε’は,大幅に改善された。興味深いことに,10³Hzで,50容積%のNCB-NPを含むナノ複合材料は,約210.8の高いε’及び低い損失正接(tanδ≒0.83)の良好な誘電特性を示す。この向上したε’値は,PVDF高分子よりも約20倍大きい。ナノ複合材料中のε’の増加は,大きな界面面積及び非常に短い粒子間距離に起因する。このことは,界面分極強度を大きく増加させる。Copyright 2016 Springer Science+Business Media New York Translated from English into Japanese by JST.