燃料電池のための四級化ポリスルホンと剥離した層状複水酸化物から誘導した陰イオン交換膜【Powered by NICT】

Anion-exchange membranes derived from quaternized polysulfone and exfoliated layered double hydroxide for fuel cells

著者 (6件)： Liu Wan (College of Materials Science and Engineering, Wuhan Textile University, WuHan 430073, PR China) ,  Liang Na (College of Materials Science and Engineering, Wuhan Textile University, WuHan 430073, PR China) ,  Peng Pai (College of Materials Science and Engineering, Wuhan Textile University, WuHan 430073, PR China) ,  Qu Rong (College of Materials Science and Engineering, Wuhan Textile University, WuHan 430073, PR China) ,  Chen Dongzhi (College of Materials Science and Engineering, Wuhan Textile University, WuHan 430073, PR China) ,  Zhang Hongwei (College of Materials Science and Engineering, Wuhan Textile University, WuHan 430073, PR China)
資料名： Journal of Solid State Chemistry  (Journal of Solid State Chemistry)
巻： 246  ページ： 324-328  発行年： 2017年 
JST資料番号： H0505A  ISSN： 0022-4596  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 層状複水酸化物(LDH)を尿素支援均一沈殿条件を制御することにより調製した。LDHsの形態と結晶性をX線回折と走査型電子顕微鏡によって確認した。LDHは四級化ポリスルホン膜に組み込まれた後,透過型電子顕微鏡を用いて,膜中のLDHシートの剥離した形態を観察した。ナノ複合材料膜の吸水性,膨潤比,機械的性質とイオン伝導率を含む特性を調べた。5%LDHシートを含むナノコンポジット膜はよりバランスのとれた性能を示し,60°Cで2.36×10~ 2Scm~ 1のイオン伝導率を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 走査電子顕微鏡 ,  *四級化 ,  沈殿 ,  *ポリスルホン ,  膨潤 ,  結晶度 ,  透過型電子顕微鏡 ,  X線回折 ,  ナノ複合材料
準シソーラス用語： ナノ複合膜 ,  イオン伝導率 ,  吸水性 ,  ポリスルフォン膜 ,  *アニオン交換膜 ,  *複水酸化物 , 【Automatic Indexing@JST】

著者キーワード (5件)： 高分子電解質膜 ,  LDH ,  Conductivity ,  アルカリ燃料電池 ,  性質

分類 (2件)： 分子化合物  (CE02000C) ,  塩基,金属酸化物  (CD01030Z)

タイトルに関連する用語 (6件)： 燃料電池 ,  四級化 ,  ポリスルホン ,  層状複水酸化物 ,  誘導 ,  陰イオン交換膜