17-4PH鋼の相の連続的核形成:ミクロ組織の特性化と機械的性質【Powered by NICT】

Sequential nucleation of phases in a 17-4PH steel: Microstructural characterisation and mechanical properties

著者 (6件)： Yeli Guma (Department of Materials, University of Oxford, Parks Road, Oxford, OX1 3PH, United Kingdom) ,  Auger Maria A. (Department of Materials, University of Oxford, Parks Road, Oxford, OX1 3PH, United Kingdom) ,  Wilford Keith (Rolls-Royce, PO Box 2000, SW1-70, Derby, DE21 7XX, United Kingdom) ,  Smith George D.W. (Department of Materials, University of Oxford, Parks Road, Oxford, OX1 3PH, United Kingdom) ,  Bagot Paul A.J. (Department of Materials, University of Oxford, Parks Road, Oxford, OX1 3PH, United Kingdom) ,  Moody Michael P. (Department of Materials, University of Oxford, Parks Road, Oxford, OX1 3PH, United Kingdom)
資料名： Acta Materialia  (Acta Materialia)
巻： 125  ページ： 38-49  発行年： 2017年 
JST資料番号： A0316A  ISSN： 1359-6454  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 高温で動作する17-4PH鋼の主要な関心事は,Feに富む(α)とCr(α′)相分離に起因する脆化,他の有害な相の析出した。本研究では17-4PH鋼における原子スケールでの微細構造変化の配列を二種の異なる時効温度480°Cおよび590°Cで原子プローブトモグラフィー(APT)により特徴づけられる。両温度での熱処理の初期段階では,APTは転位とマトリックス欠陥はNbN/CrNイオン種の偏析により明らかにされた,その後のCuリッチ析出物(CRP)とNbリッチ析出物の不均一核形成サイトを提供したことを明らかにした。低い温度では,Crリッチα’相も核形成し,最終的にMn,Ni,Siリッチ(MNS)相が生成することが観察された。,後者はより高い温度では観察されなかった,CRPとCrリッチα’相の数密度と画分の変化を定量化し,材料の全体的な析出硬化へのそれぞれの寄与を推定した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 高温 ,  析出物 ,  *核形成 ,  *鋼 ,  鉄 ,  *キャラクタリゼーション ,  数密度 ,  偏析 ,  脆化 ,  析出硬化
準シソーラス用語： 不均一核形成 ,  NbN ,  原子プローブトモグラフィー ,  原子スケール ,  *17-4PH鋼 , 【Automatic Indexing@JST】

著者キーワード (5件)： 17-4PH鋼 ,  原子プローブトモグラフィー ,  Cuリッチ析出物 ,  α′-(Cr)相 ,  析出硬化