乾燥収縮の微細構造ベースモデル化と高相対湿度におけるセメントペーストの微小亀裂【Powered by NICT】

Microstructure-based modelling of drying shrinkage and microcracking of cement paste at high relative humidity

著者 (5件)： Liu Lin (College of Civil and Transportation Engineering, Hohai University, Nanjing 210098, China) ,  Liu Lin (Jiangsu Engineering Research Center of Crack Control in Concrete, Hohai University, Nanjing 210098, China) ,  Wang Xuecheng (College of Civil and Transportation Engineering, Hohai University, Nanjing 210098, China) ,  Chen Huisu (Jiangsu Key Laboratory of Construction Materials, School of Materials Science and Engineering, Southeast University, Nanjing 211189, China) ,  Wan Chaojun (College of Materials Science and Engineering, Chongqing University, Chongqing 400044, China)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 126  ページ： 410-425  発行年： 2016年 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： セメント系材料の乾燥挙動を包括的に理解するために,本論文では,キャピラリー細孔中の水蒸発プロセス,自由境界条件をもつセメントペーストの乾燥による変形と制約の下でのセメントペーストの微小亀裂をシミュレートするために微細構造ベースモデルを提示した。Kelvin式によって定量化キャピラリー圧力効果は,初期荷重刺激であるこのモデルは高い相対湿度範囲に適用可能である。主にモデル化研究の二つの部分を行った。(1)セメントペーストHYMOSTRUC3Dの微細構造モデルから,キャピラリー細孔中の水の蒸発は,多段階ディジタル化アルゴリズムによって捕捉される。(2)異なる境界制約を有する硬化セメントペーストの乾燥収縮変形と内部微小亀裂は,3D格子破壊モデルによってシミュレートした。計算コストを低減するために,セメントペーストの微細構造とC-S-Hのナノ構造が取り込まれる場所二スケールモデリング領域を採用した。セメントペーストの自由収縮に関する実験的試験を用いて,モデルを検証することである。最後に,モデルは,多孔弾性機械的モデルと比較し,自由収縮に及ぼす水セメント比と水和時間の影響と内部微小亀裂に及ぼす制約の影響を研究するために適用した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 圧力効果 ,  *相対湿度 ,  水セメント比 ,  三次元 ,  細孔 ,  *乾燥収縮 ,  ナノ構造 ,  *セメントペースト ,  水和 ,  蒸発 ,  *微小亀裂 ,  境界条件 ,  *モデリング ,  力学モデル ,  制約条件

著者キーワード (5件)： 乾燥収縮 ,  水の蒸発 ,  微小亀裂 ,  毛管圧 ,  格子モデル