800°Cでの19%CRのNI型相ステンレス鋼の微細構造と機械的性質に及ぼすMNの影響を研究した。【JST・京大機械翻訳】

Effect of Mn on microstructure and properties of aging treatment at 800 °C of low nickel type 19%Cr duplex stainless steel

著者 (6件)： Gu Yang (Faculty of Materials Science and Engineering,Kunming University of Science and Technology) ,  Yang Yinhui (Faculty of Materials Science and Engineering,Kunming University of Science and Technology) ,  Cao Jianchun (Faculty of Materials Science and Engineering,Kunming University of Science and Technology) ,  Li Shaohong (Faculty of Materials Science and Engineering,Kunming University of Science and Technology) ,  Bai Yuliang (Faculty of Materials Science and Engineering,Kunming University of Science and Technology) ,  Lei Tingting (Faculty of Materials Science and Engineering,Kunming University of Science and Technology)
資料名： Cailiao Rechuli Xuebao  (Cailiao Rechuli Xuebao)
巻： 37  号： 8  ページ： 89-96  発行年： 2016年 
JST資料番号： C2127A  ISSN： 1009-6264  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 結果は以下を示す。MN含有量が低いとき,Σ相の析出は遅く,54時間後にフェライト粒界に分散した。MNがΣ相の形成に参与し、MN含有量が高い場合、Σ相の析出速度が速く、54H後に層状にフェライトが被覆される。MN含有量の増加は,オーステナイトの相変態を増加させ,そして,時効の初期段階は,鋼の衝撃性能を改善することができたが,しかし,時効後の多くのΣ相の析出は,衝撃性能の低下を加速した。低MN含有量の実験電位は約350MVであり,MN含有量は約200MVであり,54H後にはそれらの耐腐食性は低下した。より高いMN含有量は,時効の初期段階において,鋼の耐酸化性を向上させることができ,そして,54時間後に,それらの再酸化性は,一致する傾向があった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *鋼 ,  *微細構造 ,  耐酸化性 ,  衝撃 ,  *機械的性質 ,  オーステナイト ,  電位 ,  フェライト ,  時効 ,  *ステンレス鋼 ,  耐食性 ,  結晶粒界
準シソーラス用語： 再酸化 ,  析出速度 , 【Automatic Indexing@JST】

著者キーワード (4件)： duplex stainless steel ,  ageing microstructure ,  manganese ,  pitting corrosion resistance

分類 (3件)： 熱処理技術  (WC03020T) ,  機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (6件)： Ni ,  ステンレス鋼 ,  微細構造 ,  機械的性質 ,  Mn ,  研究