SiO_2/ZrO_2~-SiO_2複合材料のゾル-ゲルプロセスと高温特性【Powered by NICT】

Sol-gel process and high-temperature property of SiO₂/ZrO₂-SiO₂ composites

著者 (5件)： Yang Xiang (Science and Technology on Advanced Ceramic Fibers and Composites Laboratory, National University of Defense Technology, Changsha 410073, Hunan, PR China) ,  Qing Wang (Science and Technology on Advanced Ceramic Fibers and Composites Laboratory, National University of Defense Technology, Changsha 410073, Hunan, PR China) ,  Feng Cao (Science and Technology on Advanced Ceramic Fibers and Composites Laboratory, National University of Defense Technology, Changsha 410073, Hunan, PR China) ,  Yin-Wei Ma (Beijing Aerospace Technology Institute, Beijing 100074, PR China) ,  Dong-liang Quan (Beijing Aerospace Technology Institute, Beijing 100074, PR China)
資料名： Ceramics International  (Ceramics International)
巻： 43  号： 1 PA  ページ： 854-859  発行年： 2017年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： SiO_2/ZrO_2~-SiO_2複合材料をゾル-ゲル法により作製し,その高温曲げ特性を調べた。1200°Cと1500°Cでの酸化挙動も調べた。高温では,複合材料は典型的な脆性破壊を示した。SiO_2/ZrO_2~-SiO_2複合材料はSiO_2/SiO_2複合材料よりも高温で高い曲げ強さと弾性率を有していた。,ゾル-ゲル法により作製した,SiO_2/ZrO_2~-SiO_2複合材料はより高い高温寿命を示した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *ゲル ,  ゾル-ゲル法 ,  脆性破壊 ,  *高温 ,  曲げ強さ ,  *複合材料 ,  弾性係数
準シソーラス用語： 曲げ特性 ,  *高温特性 , 【Automatic Indexing@JST】

著者キーワード (4件)： ゾル-ゲル ,  複合材料 ,  高温 ,  機械的性質

分類 (2件)： セラミック・磁器の性質  (YC03030G) ,  光化学一般  (CB08010U)

タイトルに関連する用語 (4件)： 複合材料 ,  ゾル-ゲル ,  プロセス ,  高温特性