炭素繊維粉末塗装Zピンの調製とモード1剥離靭性特性に関する実験的研究【Powered by NICT】

Preparation of carbon fiber powder-coated Z-pins and experimental study on the mode I delamination toughening properties

著者 (4件)： Wang Xiao-Xu (Key Laboratory of Advanced Textile Composite Materials, Ministry of Education, Institute of Composites, Tianjin Polytechnic University, Tianjin, 300387, China) ,  Chen Li (Key Laboratory of Advanced Textile Composite Materials, Ministry of Education, Institute of Composites, Tianjin Polytechnic University, Tianjin, 300387, China) ,  Jiao Ya-Nan (Key Laboratory of Advanced Textile Composite Materials, Ministry of Education, Institute of Composites, Tianjin Polytechnic University, Tianjin, 300387, China) ,  Li Jia-Lu (Key Laboratory of Advanced Textile Composite Materials, Ministry of Education, Institute of Composites, Tianjin Polytechnic University, Tianjin, 300387, China)
資料名： Polymer Composites  (Polymer Composites)
巻： 37  号： 12  ページ： 3508-3515  発行年： 2016年 
JST資料番号： E0987A  ISSN： 0272-8397  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： z-ピンと積層板の間の接着特性を改善するために,zピンのための炭素繊維粉体塗装法を開発した。四種類のコーティング材料,1mm短いチョップド炭素繊維(CS),50メッシュ炭素繊維粉末z-ピン(CF),400メッシュ炭素繊維粉末(CP),およびカーボンナノチューブ(CN),は,z-ピンの樹脂の硬化前に含浸した繊維束上に被覆した。四タイプ被覆z-ピンの直径は0.50~0.61mm,0.57mm0.58mm,0.54mm増加した。z pin/laminateの接着特性を特性化するために,単一z-ピン引抜試験を実施した。結果は炭素繊維粉体塗装はz pin/laminateの界面接着特性を効果的に改善できることを示した。界面剪断強さは約1/3増加した。CS,CF,CPは界面の機械的インターロックと架橋効果を改善し,CNは強化モードの接着効果を増強した。強化積層板の層間性能を調べるために,二重片持梁試験を行った。,良好な界面接着特性に関係した,被覆z-ピンはZピン積層材料のモードI層間破壊靭性に対応することがわかった。Copyright 2017 Wiley Publishing Japan K.K. All Rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： *靱性 ,  被覆材 ,  *炭素繊維 ,  被覆 ,  *粉体 ,  積層材料 ,  キャラクタリゼーション ,  積層板 ,  界面 ,  *モード1 ,  引抜試験 ,  接着 ,  *粉体塗装
準シソーラス用語： 界面剪断強さ ,  界面接着 , 【Automatic Indexing@JST】

分類 (2件)： 充填剤,補強材  (YH05030J) ,  その他の高分子材料  (YH07150C)

タイトルに関連する用語 (6件)： 炭素繊維 ,  粉末塗装 ,  調製 ,  モード1 ,  靭性 ,  実験的研究