CO_2分離のためのUV開始フリーラジカル光重合により合成したポリ(エチレンオキシド)複合膜【Powered by NICT】

Poly (ethylene oxide) composite membrane synthesized by UV-initiated free radical photopolymerization for CO₂ separation

著者 (21件)： Ding Xiaoli (State Key Laboratory of Separation Membranes and Membrane Processes, Tianjin Polytechnic University, Tianjin 300387, China) ,  Ding Xiaoli (Tianjin Key Laboratory of Hollow Fiber Membrane Materials and Processes (Tianjin Polytechnic University), Tianjin 300387, China) ,  Ding Xiaoli (Institute of Separation Material and Process Control, School of Material Science and Engineering, Tianjin Polytechnic University, Tianjin 300387, China) ,  Hua MingMing (State Key Laboratory of Separation Membranes and Membrane Processes, Tianjin Polytechnic University, Tianjin 300387, China) ,  Hua MingMing (Tianjin Key Laboratory of Hollow Fiber Membrane Materials and Processes (Tianjin Polytechnic University), Tianjin 300387, China) ,  Hua MingMing (Institute of Separation Material and Process Control, School of Material Science and Engineering, Tianjin Polytechnic University, Tianjin 300387, China) ,  Zhao Hongyong (State Key Laboratory of Separation Membranes and Membrane Processes, Tianjin Polytechnic University, Tianjin 300387, China) ,  Zhao Hongyong (Tianjin Key Laboratory of Hollow Fiber Membrane Materials and Processes (Tianjin Polytechnic University), Tianjin 300387, China) ,  Zhao Hongyong (School of Environmental and Chemical Engineering, Tianjin Polytechnic University, Tianjin 300387, China) ,  Yang Pingping (State Key Laboratory of Separation Membranes and Membrane Processes, Tianjin Polytechnic University, Tianjin 300387, China) ,  Yang Pingping (Tianjin Key Laboratory of Hollow Fiber Membrane Materials and Processes (Tianjin Polytechnic University), Tianjin 300387, China) ,  Yang Pingping (Institute of Separation Material and Process Control, School of Material Science and Engineering, Tianjin Polytechnic University, Tianjin 300387, China) ,  Chen Xiaolu (State Key Laboratory of Separation Membranes and Membrane Processes, Tianjin Polytechnic University, Tianjin 300387, China) ,  Chen Xiaolu (Tianjin Key Laboratory of Hollow Fiber Membrane Materials and Processes (Tianjin Polytechnic University), Tianjin 300387, China) ,  Chen Xiaolu (Institute of Separation Material and Process Control, School of Material Science and Engineering, Tianjin Polytechnic University, Tianjin 300387, China) ,  Xin Qingping (State Key Laboratory of Separation Membranes and Membrane Processes, Tianjin Polytechnic University, Tianjin 300387, China) ,  Xin Qingping (Tianjin Key Laboratory of Hollow Fiber Membrane Materials and Processes (Tianjin Polytechnic University), Tianjin 300387, China) ,  Xin Qingping (Institute of Separation Material and Process Control, School of Material Science and Engineering, Tianjin Polytechnic University, Tianjin 300387, China) ,  Zhang Yuzhong (State Key Laboratory of Separation Membranes and Membrane Processes, Tianjin Polytechnic University, Tianjin 300387, China) ,  Zhang Yuzhong (Tianjin Key Laboratory of Hollow Fiber Membrane Materials and Processes (Tianjin Polytechnic University), Tianjin 300387, China) ,  Zhang Yuzhong (Institute of Separation Material and Process Control, School of Material Science and Engineering, Tianjin Polytechnic University, Tianjin 300387, China)
資料名： Journal of Membrane Science  (Journal of Membrane Science)
巻： 531  ページ： 129-137  発行年： 2017年 
JST資料番号： E0669A  ISSN： 0376-7388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 高CO_2透過性と高いCO_2/N_2選択性を有する複合膜はUV開始フリーラジカル光重合により合成した。支持層と選択層は光重合により作製した。支持層は単量体とポリエチレングリコールとして細孔形成添加剤としてのポリ(エチレングリコール)ジアクリレートにより合成し,一方,選択層は,ポリ(エチレングリコール)メチルエーテルアクリレート単量体とジペンタエリスリトールヘキサアクリレートとして架橋剤として合成した。複合膜の形態,化学構造とガス輸送特性を種々の方法で調べた。得られた複合膜は,38.8~40.9の範囲,高CO_2/N_2選択性をもつ無欠陥の選択層は選択層材料の固有選択性に近いを有していた。さらに,選択層の厚さと透過性は,被覆溶液の消費を変えることにより大きな影響を受けたことが分かった。選択的層の厚さは被覆溶液消費の減少とともに減少し,4.15~0.62μm,CO_2透過の有意な増加,182から1889GPU(25°C,0.2MPa)範囲につながったから。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 添加剤 ,  *ラジカル ,  支持層 ,  *光重合 ,  被覆 ,  単量体 ,  ポリエチレングリコールジアクリレート ,  *複合膜 ,  ポリエチレンオキシド
準シソーラス用語： 輸送特性 ,  化学構造 ,  細孔形成 ,  透過性 , 【Automatic Indexing@JST】

著者キーワード (5件)： 複合膜 ,  CO_2分離 ,  ポリ(エチレンオキシド) ,  架橋 ,  光重合

分類 (1件)： 膜分離  (XD02120Z)

タイトルに関連する用語 (4件)： フリーラジカル ,  光重合 ,  エチレンオキシド ,  複合膜