コバルトナノ粒子によるフェノール樹脂のカーボンナノチューブの調製【JST・京大機械翻訳】

Catalytic Preparation of Carbon Nanotubes from Phenolic Resin Using Cobalt Nanoparticle

著者 (7件)： Huang Zhenxia (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology) ,  Liang Feng (School of Chemical Engineering and Technology, Wuhan University of Science and Technology) ,  Wang Junkai (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology) ,  Zhang Haijun (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology) ,  Liu Simin (School of Chemical Engineering and Technology, Wuhan University of Science and Technology) ,  Li Saisai (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology) ,  Zhang Shaowei (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology)
資料名： Guisuanyan Xuebao  (Guisuanyan Xuebao)
巻： 44  号： 9  ページ： 1380-1386  発行年： 2016年 
JST資料番号： W1454A  ISSN： 0454-5648  CODEN： KSYHA5  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： フェノール樹脂を原料とし、硝酸コバルトを触媒前駆体とし、触媒フェノール樹脂を用いてカーボンナノチューブを合成した。カーボンナノチューブの合成に及ぼす温度と触媒量の影響を研究した。結果は以下を示す。硝酸コバルトはまずCO_3O_4に分解され、その後、その場COナノ粒子に還元され、COナノ粒子は再び炭素樹脂の熱分解により放出された炭素ガスからカーボンナノチューブを生成する。カーボンナノチューブの初期成長温度は673Kであり,最適成長温度は1Kであった。カーボンナノチューブの成長は,先端成長モードに従った。触媒の最適添加量はフェノール樹脂の質量の0.75%であった。カーボンナノチューブの直径は約20~100NMであり,長さは10ΜMであった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 先端成長 ,  熱分解 ,  *ナノ粒子 ,  触媒 ,  *フェノール樹脂 ,  前駆体 ,  *カーボンナノチューブ ,  炭素 ,  *コバルト
準シソーラス用語： 成長温度 ,  初期成長 ,  硝酸コバルト , 【Automatic Indexing@JST】