アルミナ発泡体の微細構造と性質に及ぼすミクロシリカ添加の影響【Powered by NICT】

Effects of microsilica addition on the microstructure and properties of alumina foams

著者 (5件)： Huang Keke (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology (WUST), Wuhan, 430081 PR China) ,  Li Yuanbing (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology (WUST), Wuhan, 430081 PR China) ,  Li Shujing (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology (WUST), Wuhan, 430081 PR China) ,  Wang Li (Yi Xing Hongye Insulation Engineering Co., Ltd, Yixing, 214200 PR China) ,  Wang Shihan (The State Key Laboratory of Refractories and Metallurgy, Wuhan University of Science and Technology (WUST), Wuhan, 430081 PR China)
資料名： Ceramics International  (Ceramics International)
巻： 42  号： 14  ページ： 16401-16404  発行年： 2016年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 多孔性93.3 94.4%の細胞アルミナ発泡体を溶融D-グルコース無水粉体分散の熱発泡により作製した。セラミック混合物に添加した焼結発泡体の微細構造と性質に及ぼすその影響を調べるために8wt%までのマイクロシリカ。分散は分散マイクロシリカ添加が増加するのに従って増加のずり減粘と粘度を明らかにした。マイクロシリカ添加は0から0 8wt%に増加したとき,試料は19.70%から17.82%に低下し,0.267~0.206g/cmから~3低下した試料の密度と圧縮強さの収縮は1.65から0.96MPaまで減少した。さらに,セルサイズ分布曲線は二峰性単一モードへの変換を有し,発泡体中の小窓の量は,マイクロシリカの添加により減少した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 単一モード ,  *起泡 ,  粘度 ,  *微細構造 ,  細孔径分布 ,  セラミック ,  圧縮強さ ,  多孔性 ,  焼結 ,  *アルミナ ,  粉体
準シソーラス用語： 細胞サイズ ,  ずり減粘 ,  *発泡体 , 【Automatic Indexing@JST】

著者キーワード (5件)： アルミナ ,  Foams ,  Microstructure ,  細孔径分布 ,  圧縮強さ

分類 (1件)： 耐火物  (YC04030N)

タイトルに関連する用語 (5件)： アルミナ ,  発泡体 ,  微細構造 ,  性質 ,  シリカ