J-GLOBAL ID：201702241941498193   整理番号：17A0391874

軽度アルカリおよびアルカリ酸性条件下におけるEU-1ゼオライトの修飾と逐次処理【Powered by NICT】

Modification and sequential treatment of EU-1 zeolite in mild alkali and alkaline-acid conditions

著者 (7件)： Li Xiaofeng (Research Institute of Special Chemicals, Taiyuan University of Technology) ,  Sun Xiaotao (Research Institute of Special Chemicals, Taiyuan University of Technology) ,  Zhang Yanting (Research Institute of Special Chemicals, Taiyuan University of Technology) ,  Zhang Junliang (China University of Petroleum-Beijing Changping(beijing)) ,  Ren Pengchao (Research Institute of Special Chemicals, Taiyuan University of Technology) ,  Liu Xiaozhen (Research Institute of Special Chemicals, Taiyuan University of Technology) ,  Dou Tao (Research Institute of Special Chemicals, Taiyuan University of Technology)
資料名： Chinese Journal of Chemical Engineering  (Chinese Journal of Chemical Engineering)
巻： 24  号： 12  ページ： 1728-1734  発行年： 2016年 
JST資料番号： W0620A  ISSN： 1004-9541  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 英語 (EN)

抄録/ポイント： EU-1ゼオライトを低濃度炭酸ナトリウム(Na_2CO_3)と塩酸(HCl)溶液で処理した。得られた試料をX線回折(XRD),走査電子顕微鏡(SEM),N2吸着/脱着,NH_3の昇温脱離(NH(3 )TPD),固体状態(27)Al核磁気共鳴((27)Al NMR)によって特性化し,処理した試料の触媒性能をキシレン異性化反応で試験した。結果は0.05モルL 1( 1)Na_2CO_3と0.1mol/L( 1)HCl溶液で処理した連続的に試料の外部表面積とメソ細孔容積は73.9m~2g ( 1)と0.162cm~3g ( 1)に達したことを示した。EU-1ゼオライトの触媒性能が大幅に改善され,プローブ反応の活性は23.03%から23.61%に増加し,選択性は親試料のそれと比較して85.09%から87.14%に増加したことを示した。さらに,非晶質シリカとアルミナ種のみが後処理プロセス中に溶解したが,骨格構造とEU-1ゼオライトの酸性特性は無傷のままであったことが分かった。Data from the ScienceChina, LCAS. Translated by JST【Powered by NICT】

シソーラス用語： 表面積 ,  昇温脱離 ,  炭酸ナトリウム ,  アルミナ ,  触媒活性 ,  走査電子顕微鏡 ,  固相 ,  後処理 ,  異性化 ,  塩酸 ,  *酸性 ,  *シーケンシャル処理
準シソーラス用語： 非晶質シリカ ,  メソ孔 ,  キシレン , 【Automatic Indexing@JST】

著者キーワード (3件)： EU-1ゼオライト ,  メソ多孔性 ,  Catalysis

分類 (1件)： その他の触媒  (CB06123Z)

タイトルに関連する用語 (7件)： 軽度 ,  アルカリ ,  酸性条件 ,  Eu ,  ゼオライト ,  修飾 ,  逐次処理