固化湖沼泥土層の性能と微細構造【JST・京大機械翻訳】

Performance and Micro-structure of Fired Bricks Made of Solidified Lake Silt

著者 (6件)： Zhang Yamei (Jiangsu Key Laboratory of Construction Materials, School of Materials Science and Engineering, Southeast Univ) ,  Jia Lutao (Jiangsu Key Laboratory of Construction Materials, School of Materials Science and Engineering, Southeast Univ) ,  Cui Qiang (Wuxi Guolian Environment Energy Group Co, Ltd) ,  Mei Hao (Jiangsu Key Laboratory of Construction Materials, School of Materials Science and Engineering, Southeast Univ) ,  Zhang Peigen (Jiangsu Key Laboratory of Construction Materials, School of Materials Science and Engineering, Southeast Univ) ,  Sun Zhengming (Jiangsu Key Laboratory of Construction Materials, School of Materials Science and Engineering, Southeast Univ)
資料名： Hunan Daxue Xuebao. Ziran Kexue Ban  (Hunan Daxue Xuebao. Ziran Kexue Ban)
巻： 43  号： 12  ページ： 56-61  発行年： 2016年 
JST資料番号： W0616A  ISSN： 1674-2974  CODEN： HDAXE3  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： 主原料として固化したスラッジを用いて,真空押出成形技術によって調製し,焼結した。原料の物理化学的性質の分析により、少量の硬化剤の添加は、泥の塑性指数、酸化物の組成、鉱物組成などを明らかに変化させないが、成形性能に一定の影響を与えることが分かった。実験を行い,湖沼泥土,固化泥土の実験室におけるサンプルの乾燥線形収縮,焼結後の小様Zhuanの体積密度,吸水率,強度,熱伝導率,耐凍性などを比較した。研究により、硬化泥の含有量が90%、石炭含有量が10%の時、制備出Piの乾燥収縮率は%%、製品の吸水率は18.2%、強度は15.8MPAの小様Zhuanであり、その総合的な性能は未処理の湖沼スラッジの焼結率よりやや低いことが分かった。SEMとMIPを用いて,微細構造を研究し,その結果によると,固化したスラッジの微細構造は,同じ炭素含有量の湖沼スラッジと比較して,より小さく,ガラス相で被覆されていない粒子と未充填の孔隙がより多かった。多孔度が大きいと、その強度が低く、吸水率が高い主な原因であるが、同時に、その熱伝導率はやや低く、2種類の焼結助剤はいずれも良好な耐凍性を有する。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： *湖沼 ,  焼結 ,  鉱物組成 ,  *微細構造 ,  空隙率 ,  吸水率 ,  成形性 ,  スラッジ ,  熱伝導率 ,  *凝固 ,  押出成形 ,  耐凍性
準シソーラス用語： 焼結助剤 ,  塑性指数 ,  物理化学的性質 , 【Automatic Indexing@JST】

著者キーワード (5件)： lake silt ,  solidified lake silt ,  fired brick ,  microstructure ,  strength

分類 (1件)： セラミック・陶磁器の製造  (YC03020V)

タイトルに関連する用語 (5件)： 固化 ,  湖沼 ,  泥 ,  土層 ,  微細構造