MG-13GD-4Y-2ZN-0.5ZRマグネシウム合金の圧縮過程の動的再結晶【JST・京大機械翻訳】

Dynamic recrystallization of Mg-13Gd-4Y-2Zn-0.5Zr alloy during hot compression

著者 (5件)： Qi Hongna (College of Materials Science and Engineering,North University of China, Engineering Technology Research Center for Integrated Precision Forming of Shanxi) ,  Zhang Zhimin (College of Materials Science and Engineering,North University of China, Engineering Technology Research Center for Integrated Precision Forming of Shanxi) ,  Yu Jianmin (College of Materials Science and Engineering,North University of China, Engineering Technology Research Center for Integrated Precision Forming of Shanxi) ,  Yin Xueyan (College of Materials Science and Engineering,North University of China, Engineering Technology Research Center for Integrated Precision Forming of Shanxi) ,  Yu Xiang (North General Power Group CO.,LTD)
資料名： Bingqi Cailiao Kexue yu Gongcheng  (Bingqi Cailiao Kexue yu Gongcheng)
巻： 39  号： 6  ページ： 83-87  発行年： 2016年 
JST資料番号： C2398A  ISSN： 1004-244X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： MG-13GD-4Y-2ZN-0.5ZR合金の動的再結晶化挙動を研究するために,350~500°Cの歪速度と0.001~1.000S(-1)の歪速度範囲で,動的再結晶を研究した。GLEEBLE3500を用いて合金の圧縮実験を行い、XRDと金属顕微鏡を用いて変形後の合金組織を分析した。結果は以下を示す。合金は均質化し,主相はMGマトリックス及び析出相W相(MG_3Y_2ZN_3),I相(MG_3YZN_6)及び長距離秩序相(MG_(12)YZN)であり,変形過程中に長距離秩序相が残っている。MG-13GD-4Y-2ZN-0.5ZR合金の熱圧縮曲線は典型的な動的再結晶型であり,ピーク応力は歪速度の低下と温度の上昇とともに減少した。歪速度の増加と温度の上昇とともに,動的再結晶は結晶粒内に広がり,組織成分は均一になった。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 金属顕微鏡 ,  *合金 ,  均質化 ,  結晶粒 ,  歪速度 ,  *マグネシウム合金 ,  X線回折 ,  長範囲規則度 ,  *動的再結晶
準シソーラス用語： 圧縮曲線 ,  I相 , 【Automatic Indexing@JST】

著者キーワード (4件)： hot-compression ,  XRD ,  strain-stress curve ,  dynamic recrystallization

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (3件)： マグネシウム合金 ,  過程 ,  動的再結晶