C/C複合材料の熱衝撃と内部摩擦【Powered by NICT】

Internal friction vs. thermal shock in C/C composites

著者 (5件)： Liu Yue (State Key Laboratory of Solidification Processing, Carbon/Carbon Composites Research Center, Northwestern Polytechnical University, Xi’an, Shaanxi 710072, PR China) ,  Fu Qiangang (State Key Laboratory of Solidification Processing, Carbon/Carbon Composites Research Center, Northwestern Polytechnical University, Xi’an, Shaanxi 710072, PR China) ,  Zhao Fengling (State Key Laboratory of Solidification Processing, Carbon/Carbon Composites Research Center, Northwestern Polytechnical University, Xi’an, Shaanxi 710072, PR China) ,  Sun Guodong (State Key Laboratory of Solidification Processing, Carbon/Carbon Composites Research Center, Northwestern Polytechnical University, Xi’an, Shaanxi 710072, PR China) ,  Li Hejun (State Key Laboratory of Solidification Processing, Carbon/Carbon Composites Research Center, Northwestern Polytechnical University, Xi’an, Shaanxi 710072, PR China)
資料名： Composites. Part B. Engineering  (Composites. Part B. Engineering)
巻： 106  ページ： 59-65  発行年： 2016年 
JST資料番号： W0437B  ISSN： 1359-8368  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 炭素/炭素(C/C)複合材料の熱疲労挙動を理解するために,異なる時間1373Kと室温の間の熱サイクルに供した。熱サイクル後の微細構造,機械的強度および内部摩擦を研究した。結果は,C/C複合材料の曲げ強さは1373Kと室温の間の熱サイクル10回後でも69MPaから89MPaに増加した,内部摩擦は,熱サイクルの増加と共に有意に増加したことを示した。内部摩擦と強度の改善は,界面での残留熱応力の増加に起因していた。熱サイクルの更なる増加は,マトリックス亀裂と界面結合強度の低下に起因する炭素マトリックスと繊維の間の界面強度を減少させるであろう。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 熱サイクル ,  界面 ,  *熱衝撃 ,  炭素 ,  微細構造 ,  *内部摩擦 ,  機械的強度 ,  亀裂 ,  曲げ強さ ,  *C/C複合材料 ,  付着強さ
準シソーラス用語： 界面強度 ,  熱残留応力 ,  疲労挙動 , 【Automatic Indexing@JST】