簡単な圧延により加工したAl-Mg-Sc-Zr合金の高歪速度超塑性【Powered by NICT】

High strain rate superplasticity in an Al-Mg-Sc-Zr alloy processed via simple rolling

著者 (5件)： Li Mengjia (School of Materials Science and Engineering, Central South University, Changsha 410083, China) ,  Pan Qinglin (Nonferrous Metal Oriented Advanced Structural Materials and Manufacturing Cooperative Innovation Center, Central South University, Changsha 410083, China) ,  Shi Yunjia (School of Materials Science and Engineering, Central South University, Changsha 410083, China) ,  Sun Xue (School of Materials Science and Engineering, Central South University, Changsha 410083, China) ,  Xiang Hao (School of Materials Science and Engineering, Central South University, Changsha 410083, China)
資料名： Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing  (Materials Science & Engineering. A. Structural Materials: Properties, Microstructure and Processing)
巻： 687  ページ： 298-305  発行年： 2017年 
JST資料番号： D0589B  ISSN： 0921-5093  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 標準ゲージサイズ(18mm by 6mm)とAl-Mg-Sc-Zr試料の超塑性挙動は単純な圧延を用いて調製し,1.67×10~ 3s~ 1から1×10~ 1s~ 1の範囲の歪速度で450°Cから525°Cの温度範囲で試験した。適切な変形パラメータを用いて,Al-Mg-Sc-Zr合金は300%よりはるかに高い破断伸びを有し,最大伸びは740%であった。光学顕微鏡(OM)と透過電子顕微鏡(TEM)を用いて微細構造と転位下部組織研究は動的再結晶を明らかにした。超塑性の変形機構に及ぼす粒径と活性化エネルギーを検討した。結果はまた,これらのナノスケールAl_3(Sc_1 xZr_x)粒子を超塑性過程において重要な役割を果たすことを示した。Al_6FeMn粒子は,空洞の形成と成長,試験片の破壊に導くことができるを誘導することが分かった。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 下部組織 ,  活性化エネルギー ,  動的再結晶 ,  変形パラメータ ,  透過型電子顕微鏡 ,  *歪速度 ,  粒径 ,  伸び ,  *超塑性
準シソーラス用語： ナノスケール ,  変形機構 ,  破断伸び ,  温度範囲 ,  *高ひずみ速度 , 【Automatic Indexing@JST】

著者キーワード (4件)： Superplasticity ,  Al-Mg合金 ,  Sc ,  動的再結晶