ペロブスカイト型酸化物(LA_(0.9)EU_(0.1))_(4/3)SR_(5/3)MN_2O_7の磁気的および電気的性質を研究した。【JST・京大機械翻訳】

Magnetic and Transport Properties of Bilayered Perovskite Manganites(La_(0.9)Eu_(0.1))_(4 /3)Sr_(5 /3)Mn_2O_7

著者 (8件)： Wan Sulei (School of Physical Science and Technology,Baotou Teachers’ College) ,  Wang Zhiguo (School of Physical Science and Technology,Baotou Teachers’ College) ,  Xiang Junyou (School of Physical Science and Technology,Baotou Teachers’ College) ,  Wu Kehan (School of Physical Science and Technology,Baotou Teachers’ College) ,  Zhang Xuefeng (Inner Mongolia Key Laboratory of Magnetism and Magnetic Materials) ,  Lu Yi (Inner Mongolia Key Laboratory of Magnetism and Magnetic Materials) ,  Zhao Jianjun (Inner Mongolia Key Laboratory of Magnetism and Magnetic Materials) ,  Wang Fang (School of Physical Science and Technology,Baotou Teachers’ College)
資料名： Xitu  (Xitu)
巻： 37  号： 5  ページ： 88-91  発行年： 2016年 
JST資料番号： C2057A  ISSN： 1004-0277  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： LA_(0.9)EU_(0.1))_(4/3)SR_(5/3)MN_2O_7多結晶試料を従来の固相反応法によって調製した。XRDによると,LA_(0.9)EU_(0.1))_(4/3)SR_(5/3)MN_2O_7は,良好な熱安定性を示した。温度変化(M-T)と磁化強度は,温度変化とともに,磁場変化曲線(M-H)と電子スピン共鳴(ESR)スペクトルによって,温度の上昇とともに増加することが分かった。サンプルは三次元長距離強磁性転移点(T_C(3D)≒75K)と二次元短距離強磁性秩序転移点(T_C(2D)≒227K)を経験し,T_C(3D)とT_C(2D)の間で強磁性と常磁性状態を示した。温度が360Kに達すると,純順磁態は,低温領域(T_C(3D)以下)において,類団簇スピンガラスの特性を示した。磁気抵抗の温度変化による-曲線は,T≒84K付近で試料が最大磁気抵抗を示した。さらに,(LA_(0.9)EU_(0.1))_(4/3)SR_(5/3)MN_2O_7の熱伝導率曲線を用いて,高温領域におけるサンプルの熱伝導モデルを得た。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 温度変動 ,  常磁性 ,  固相反応 ,  熱伝導率 ,  *磁気 ,  X線回折 ,  二次元 ,  スピンガラス ,  強磁性 ,  熱安定性 ,  熱伝導 ,  ESR【磁気共鳴】 ,  多結晶 ,  磁気抵抗 ,  転移温度

著者キーワード (4件)： magnetic property ,  electrical property ,  spin glass ,  ESR

分類 (2件)： 金属結晶の磁性  (BM06040T) ,  酸化物結晶の磁性  (BM06050E)

タイトルに関連する用語 (5件)： ペロブスカイト ,  酸化物 ,  磁気 ,  電気的性質 ,  研究