マグネシウム合金における双晶の迅速硬化と疲労について【Powered by NICT】

On the rapid hardening and exhaustion of twinning in magnesium alloy

著者 (6件)： Wu P.D. (Department of Mechanical Engineering, McMaster University Hamilton, Ontario L8S 4L7, Canada) ,  Guo X.Q. (State Key Laboratory for Geomechanics and Deep Underground Engineering China University of Mining and Technology, Xuzhou, Jiangsu 221116, China) ,  Qiao H. (Department of Mechanical Engineering, McMaster University Hamilton, Ontario L8S 4L7, Canada) ,  Agnew S.R. (Department of Materials Science and Engineering, University of Virginia, Charlottesville, VA, USA) ,  Lloyd D.J. (Aluminum Materials Consultants, 106 Nicholsons Point Road, Bath, Ontario K0H 1G0, Canada) ,  Embury J.D. (Department of Materials Science and Engineering, McMaster University Hamilton, Ontario L8S 4L7, Canada)
資料名： Acta Materialia  (Acta Materialia)
巻： 122  ページ： 369-377  発行年： 2017年 
JST資料番号： A0316A  ISSN： 1359-6454  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 急速硬化と双晶支配条件下でのマグネシウム合金における双晶の消耗の可能な役割,大歪弾性粘塑性自己無撞着モデルに基づいて数値的に調べた。引張双晶の枯渇により,更なる変形は,材料がプリズム面及びピラミッド滑り,相対的に高い臨界分解せん断応力(CRSS)を活性化する必要があることが分かった。しかし,引張双晶の消耗での応力レベルは,プリズム面及びピラミッド滑りを活性化するのに十分ではない。その結果,課された歪増分は主に弾性変形によって調節されなければならず,歪硬化速度は,弾性率の大部分となっている。,急速硬化は材料の大きな体積分率の弾性と関連のある多くの複合応答,通常金属の歪硬化の原因となる転位-転位相互作用よりもであると結論できる。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： 粘塑性 ,  多結晶 ,  臨界 ,  *双晶 ,  引張 ,  剪断応力 ,  高速度 ,  体積率 ,  プリズム ,  弾性変形 ,  弾性 ,  角錐 ,  *マグネシウム合金 ,  歪硬化
準シソーラス用語： 転位相互作用 , 【Automatic Indexing@JST】

著者キーワード (4件)： 双晶化 ,  硬化 ,  多結晶塑性モデル化 ,  マグネシウム合金

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (4件)： マグネシウム合金 ,  双晶 ,  硬化 ,  疲労