CO_2/水溶液中での20鋼の腐食挙動を研究した。【JST・京大機械翻訳】

Corrosion behavior of 20 steel in liquid medium of gas-liquid(CO_2-water) stratified flow

著者 (5件)： Song Wenming (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals,Lanzhou University of Technology) ,  Yang Guirong (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals,Lanzhou University of Technology) ,  Feng Pingping (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals,Lanzhou University of Technology) ,  Ma Ying (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals,Lanzhou University of Technology) ,  Hao Yuan (State Key Laboratory of Advanced Processing and Recycling of Nonferrous Metals,Lanzhou University of Technology)
資料名： Cailiao Rechuli Xuebao  (Cailiao Rechuli Xuebao)
巻： 37  号： 9  ページ： 118-123  発行年： 2016年 
JST資料番号： C2127A  ISSN： 1009-6264  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： SEM,XRD,EDSを用いて,CO_2/水溶液中での20鋼の腐食速度,腐食形態,腐食生成物の組成を研究し,腐食挙動を分析した。結果は以下を示す。20鋼の腐食速度は時間の延長とともに規則的に変化し,腐食速度のピーク値は4時間と8時間でそれぞれ2.27MM/Aと1.66MM/Aであった。5時間と12時間の腐食速度は1.02MM/Aであり,腐食生成物の厚さは約6ΜMで,厚さは約6ΜMであり,腐食生成物の主成分はFE,C,Oであった。内層生成物膜中のFE、CとO原子の比は安定しているが、外層の生成物層のFE、CとO原子の比は膜の厚さ方向に大きく変化する。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 腐食速度 ,  *鋼 ,  *腐食 ,  腐食生成物 ,  X線回折 ,  ピーク値 ,  *水溶液
準シソーラス用語： *腐食挙動 , 【Automatic Indexing@JST】

著者キーワード (5件)： 20 steel ,  gas-liquid stratified flow ,  corrosion morphology ,  corrosion products ,  corrosion mechanism