アンモニアの選択的接触酸化のためのPt/ZrO_2触媒へのW添加による触媒性能の促進【Powered by NICT】

Promotion of catalytic performance by adding W into Pt/ZrO₂ catalyst for selective catalytic oxidation of ammonia

著者 (6件)： Sun Mengmeng (Institute of New Energy and Low-Carbon Technology, Sichuan University, Chengdu 610064, Sichuan, China) ,  Wang Suning (College of Chemical Engineering, Sichuan University, Chengdu 610064, Sichuan, China) ,  Li Yuanshan (College of Chemical Engineering, Sichuan University, Chengdu 610064, Sichuan, China) ,  Xu Haidi (Institute of New Energy and Low-Carbon Technology, Sichuan University, Chengdu 610064, Sichuan, China) ,  Chen Yaoqiang (Institute of New Energy and Low-Carbon Technology, Sichuan University, Chengdu 610064, Sichuan, China) ,  Chen Yaoqiang (College of Chemical Engineering, Sichuan University, Chengdu 610064, Sichuan, China)
資料名： Applied Surface Science  (Applied Surface Science)
巻： 402  ページ： 323-329  発行年： 2017年 
JST資料番号： B0707B  ISSN： 0169-4332  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： Pt WO_3/ZrO_2触媒はPt/ZrO_2のアンモニア酸化性能を向上させるために,共含浸法により調製した。組織,構造,表面化学状態,酸化還元特性と酸特性,Pt/ZrO_2及びPt WO_3/ZrO_2触媒の触媒性能と共に差異を系統的に調べた。H_2TPRの結果は,白金上へのタングステンの影響によるPt/ZrO_2のそれよりもPt WO_3/ZrO_2により保持された高い還元能が向上することが明らかになった。XPSの結果は,白金種へのタングステンからの電子移動は,白金周辺の高い電子密度を行ったことを示した。TEMの結果は,活性格子面Pt[111]は,W種の改質によって得られたことを明らかにした。Pt WO_3/ZrO_2はPt/ZrO_2と比較して明らかに良好なアンモニア酸化性能を示し,NH_3のライトオフ温度は284°Cから249°Cにシフトし,活性化エネルギーは113.4kJmol~ 1から96.2kJmol~ 1に減少した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： タングステン ,  *接触酸化 ,  電子密度 ,  含浸 ,  還元性 ,  *触媒 ,  活性化エネルギー ,  界面化学 ,  *白金 ,  *触媒活性 ,  *アンモニア ,  電子移動
準シソーラス用語： 酸化還元特性 ,  アンモニア酸化 , 【Automatic Indexing@JST】

著者キーワード (5件)： アンモニア酸化 ,  白金 ,  タングステン ,  還元能力 ,  格子面

分類 (2件)： 貴金属触媒  (CB06122I) ,  その他の触媒  (CB06123Z)

タイトルに関連する用語 (6件)： アンモニア ,  接触酸化 ,  Pt ,  触媒 ,  触媒性能 ,  促進