TiB_2 ZrB_2とTiB_2 ZrB_2/Ni層で被覆した電極の比較故障解析【Powered by NICT】

Comparative failure analysis of electrodes coated with TiB₂-ZrB₂ and TiB₂-ZrB₂/Ni layers

著者 (18件)： Luo Ping (Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan 430068, China) ,  Luo Ping (School of Materials and Chemical Engineering, Hubei University of Technology, Wuhan 430068, China) ,  Xiong Can (Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan 430068, China) ,  Xiong Can (School of Materials and Chemical Engineering, Hubei University of Technology, Wuhan 430068, China) ,  Wang Chong (Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan 430068, China) ,  Wang Chong (School of Materials and Chemical Engineering, Hubei University of Technology, Wuhan 430068, China) ,  Qin Fucheng (Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan 430068, China) ,  Qin Fucheng (School of Materials and Chemical Engineering, Hubei University of Technology, Wuhan 430068, China) ,  Xiao Yao (Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan 430068, China) ,  Xiao Yao (School of Materials and Chemical Engineering, Hubei University of Technology, Wuhan 430068, China) ,  Li Zhi (Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan 430068, China) ,  Li Zhi (School of Materials and Chemical Engineering, Hubei University of Technology, Wuhan 430068, China) ,  Liu Kang (Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan 430068, China) ,  Liu Kang (School of Materials and Chemical Engineering, Hubei University of Technology, Wuhan 430068, China) ,  Guan Xu (Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan 430068, China) ,  Guan Xu (School of Materials and Chemical Engineering, Hubei University of Technology, Wuhan 430068, China) ,  Dong Shijie (Hubei Provincial Key Laboratory of Green Materials for Light Industry, Hubei University of Technology, Wuhan 430068, China) ,  Dong Shijie (School of Materials and Chemical Engineering, Hubei University of Technology, Wuhan 430068, China)
資料名： Surface & Coatings Technology  (Surface & Coatings Technology)
巻： 317  ページ： 83-94  発行年： 2017年 
JST資料番号： D0205C  ISSN： 0257-8972  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： モノリシックTiB_2 ZrB_2被覆電極と同様に多層TiB_2 ZrB_2/Ni被覆は抵抗スポット溶接(RSW)Znめっき鋼に使用された,溶接中の被覆の破壊挙動を調べた。走査電子顕微鏡(SEM),エネルギー分散X線分光法(EDX),X線回折分析(XRD),微小硬さ測定は,コーティングの微細構造,シートのZnを被覆した電極の反応,合金層の形成を特性化した。保護被覆は,その先端での塑性変形を抑制し,このようにして侵食過程を遅くすることによりRSW電極の表面硬さを著しく改善したことが分かった。さらに,ZrB_2TiB_2被覆とZrB_2 TiB_2/Ni被覆電極は異なる破壊機構を示した。合金化効果と塑性変形の組合せはZrB_2TiB_2被覆電極の最終的な破壊を引き起こしたが,ZrB_2 TiB_2/Ni被覆電極は,塑性変形を主ににより失敗した。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： エネルギー分散X線分光分析 ,  *被覆 ,  微細構造 ,  溶接 ,  塑性変形 ,  亜鉛めっき ,  合金化 ,  亜鉛 ,  被覆溶接棒 ,  X線回折 ,  合金層 ,  走査電子顕微鏡 ,  微小硬さ
準シソーラス用語： 破壊機構 , 【Automatic Indexing@JST】

著者キーワード (4件)： チタンdiboride-ジルコニウム二ほう化 ,  故障解析 ,  銅合金電極 ,  被覆

分類 (2件)： 固体の機械的性質一般  (BL01021C) ,  金属材料へのセラミック被覆  (YC02050V)

タイトルに関連する用語 (2件)： Ni層 ,  故障解析