低合金鋼と合金82溶接金属の間の異種金属溶接のミクロ組織と硬さの研究【Powered by NICT】

Microstructural and hardness investigations on a dissimilar metal weld between low alloy steel and Alloy 82 weld metal

著者 (5件)： Chen Z.R. (National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083, China) ,  Lu Y.H. (National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083, China) ,  Ding X.F. (National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083, China) ,  Shoji T. (National Center for Materials Service Safety, University of Science and Technology Beijing, Beijing 100083, China) ,  Shoji T. (Fracture and Reliability Research Institute, Tohoku University, 6-6-01, Aramaki Aoba, Aoba-ku, Sendai City 980-8579, Japan)
資料名： Materials Characterization  (Materials Characterization)
巻： 121  ページ： 166-174  発行年： 2016年 
JST資料番号： D0448C  ISSN： 1044-5803  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 低合金鋼(LAS)A508IIIと合金82溶接金属(WM)の間の異種金属溶接(DMW)の溶融境界(FB)領域でのミクロ組織と硬さに関する研究を行った。結果はFBs,マルテンサイトFBと鋭いFBの二種で,明らかに異なるミクロ組織,同じFBに分布交互にあることを示した。マルテンサイトFB領域は以前の大きなオーステナイト粒とFBを横切る元素濃度,高い長さ/幅比を持つ柱状WM粒,厚いマルテンサイト層と広い熱影響部(HAZ)の緩やかな変化を示した。比較により,鋭いFB領域はFBを横切る元素濃度の比較的急激な変化,低長さ/幅比を持つWM結晶粒とより小さい前オーステナイト結晶粒を持つ狭いHAZを有していた。マルテンサイトはWM粒との間にK-S方位関係を持っていたが,方位関係は鋭いFBでHAZ粒とWM結晶粒の間では認められなかった。鋭いFBと比較してはマルテンサイトFBにHAZではるかにΣ3境界であった。マルテンサイトFBの最大硬度は非常にシャープであったFBのそれよりはるかに高く,これはマルテンサイトFBでマルテンサイト層に起因していた。Copyright 2017 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【Powered by NICT】

シソーラス用語： マルテンサイト ,  *溶接金属 ,  オーステナイト ,  *異種金属溶接 ,  結晶粒 ,  *低合金鋼 ,  *硬度 ,  *合金

著者キーワード (5件)： 異種金属溶接部 ,  マルテンサイト核融合境界 ,  鋭い融合境界 ,  Microstructure ,  Hardness

分類 (2件)： 溶接部  (WC07100I) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (7件)： 低合金鋼 ,  合金 ,  溶接金属 ,  異種金属溶接 ,  ミクロ組織 ,  硬さ ,  研究