中性および酸性溶液中でのQ235炭素鋼の表面におけるフィチン酸化成皮膜の腐食挙動を研究した。【JST・京大機械翻訳】

Corrosion Inhibition Effect of Phytic Acid Conversion Coating Formed on Q235 Carbon Steel in Acidic and Neutral Solutions

著者 (6件)： Hao Yongsheng (School of Materials Science and Engineering, Shenyang University of Chemical Technology) ,  Sani Luqman Abdullahi (School of Materials Science and Engineering, Shenyang University of Chemical Technology) ,  Song Lixin (School of Materials Science and Engineering, Shenyang University of Chemical Technology) ,  Xu Guobao (Changchun Institute of Applied Chemistry, Chinese Academy of Sciences) ,  Ge Tiejun (School of Materials Science and Engineering, Shenyang University of Chemical Technology) ,  Fang Qinghong (School of Materials Science and Engineering, Shenyang University of Chemical Technology)
資料名： Zhongguo Fushi yu Fanghu Xuebao  (Zhongguo Fushi yu Fanghu Xuebao)
巻： 36  号： 6  ページ： 549-558  発行年： 2016年 
JST資料番号： W0862A  ISSN： 1005-4537  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： フィチン酸化成皮膜を中性および酸性フィチン酸溶液中で調製し,その耐食性を研究した。その結果,中性フィチン酸溶液中で得られたフィチン酸化成皮膜の耐食性は酸性溶液中で得られたフィチン酸化成皮膜より優れており,特に0.06MOL/L,PH7.0のフィチン酸溶液中で1時間フィチン酸化成皮膜とQ235炭素鋼電極表面は物理吸着により結合しているが,それには優れた界面接着力がある。XPS結果は,フィチン酸が不動態炭素鋼の表面に機能することを示して,最終的に,炭素鋼の表面におけるフィチン酸化成皮膜は,フィチン酸化成皮膜と炭素鋼表面のFE_2O両者は相乗的抑制作用により炭素鋼電極が外部腐食媒体の浸食を受けないことを保護する。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 不動態 ,  *化成皮膜 ,  *炭素鋼 ,  物理吸着 ,  腐食 ,  *酸性 ,  耐食性 ,  糖アルコール ,  イノシトールリン酸
準シソーラス用語： 抑制効果 ,  界面接着 ,  電極表面 ,  *腐食挙動 ,  *Q235 ,  *酸性溶液 ,  *中性 , 【Automatic Indexing@JST】

著者キーワード (6件)： Q235 carbon steel ,  conversion coating ,  polarization curve ,  phytic acid ,  EIS ,  XPS

分類 (2件)： 化成処理  (WC08050J) ,  防食  (WB03040M)

物質索引 (1件)： フィチン酸

タイトルに関連する用語 (8件)： 中性 ,  酸性溶液 ,  Q235 ,  炭素鋼 ,  フィチン酸 ,  化成皮膜 ,  腐食挙動 ,  研究