AL-20SI合金のミクロ組織と摩耗特性を,スプレーフォーミングによって連続的に押出した。【JST・京大機械翻訳】

Microstructure and Wear Performance of Al-20Si Alloy Prepared by Spray Deposition and Conform

著者 (6件)： Li Hao (Faculty of Materials Science and Engineering,Kunming University of Science and Technology) ,  Yin Jiancheng (Faculty of Materials Science and Engineering,Kunming University of Science and Technology) ,  Wang Yufeng (Faculty of Materials Science and Engineering,Kunming University of Science and Technology) ,  Zhang Junyi (Faculty of Materials Science and Engineering,Kunming University of Science and Technology) ,  Zhang Chao (Faculty of Materials Science and Engineering,Kunming University of Science and Technology) ,  Zhong Yi (Faculty of Materials Science and Engineering,Kunming University of Science and Technology)
資料名： Cailiao Kexue Yu Gongcheng Xuebao  (Cailiao Kexue Yu Gongcheng Xuebao)
巻： 34  号： 2  ページ： 296-300  発行年： 2016年 
JST資料番号： C2657A  ISSN： 1673-2812  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： 中国 (CHN)  言語： 中国語 (ZH)

抄録/ポイント： スプレーフォーミング連続押出技術はスプレーフォーミングと連続押出による新しい技術である。本研究では、自作のスプレー堆積連続押出設備を用いて、多種の過熱条件下でAL-20SI合金のスプレー堆積連続押出試験を行い、Μ8MMのアルミニウム合金部品を得て、それぞれそのミクロ組織と摩擦摩耗性能について研究した。結果は以下を示す。スプレーフォーミングの連続押出は,SIの核形成と成長を効果的に抑制することができ,SI-AL合金の粒径は約3~8ΜMであり,その微細構造は明らかに微細化し,耐摩耗性は1~2倍に増加した。熱間押出の増加とともに,連続押出AL-SI合金中のSI-SI合金のサイズは減少し,そして,分布はより分散し,そして,合金の耐摩耗性は,より優れていた。Data from the ScienceChina, LCAS. Translated by JST【JST・京大機械翻訳】

シソーラス用語： 微細構造 ,  *摩耗特性 ,  *摩耗 ,  精密化 ,  *スプレーフォーミング ,  核形成 ,  耐摩耗性 ,  過熱 ,  粒径 ,  *合金 ,  熱間押出 ,  アルミニウム合金

著者キーワード (5件)： hypereutectic Al-Si alloy ,  spray deposition and Conform ,  overheating treatment ,  wear and tribology ,  microstructure

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (4件)： ミクロ組織 ,  摩耗特性 ,  スプレーフォーミング ,  押出